impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	55 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	65 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	55 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	55 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.8mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	750 °C
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	21 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus 23°C	ISO 178/A	10300 Mpa
bending strength	bending strength 23°C	ASTM D790	207 Mpa
bending strength	bending strength	bending strength 23°C	ISO 178	230 Mpa
Bending strain	Bending strain 23°C		3.0 %
Tensile modulus	Tensile modulus 23°C	ASTM D638	9980 Mpa
Tensile modulus	Tensile modulus	Tensile modulus 23°C	ISO 527-2/1	10400 Mpa
tensile strength	tensile strength Break,23°C	ASTM D638	123 Mpa
tensile strength	tensile strength	tensile strength Break,23°C	ISO 527-2/5	145 Mpa
elongation	elongation Break,23°C	ASTM D638	2.5 %
Tensile strain	Tensile strain Break,23°C	ISO 527-2/5	2.8 %
Tensile creep modulus	Tensile creep modulus 1hr	ISO 899-1	10000 Mpa
Tensile creep modulus	Tensile creep modulus	Tensile creep modulus 1000hr	ISO 899-1	8500 Mpa
Bending modulus	Bending modulus 23°C	ASTM D790	8550 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
TemperatureIndex	TemperatureIndex 介电强度	IEC 60216	155
	TemperatureIndex	TemperatureIndex 拉伸冲击强度	IEC 60216	140
	TemperatureIndex	TemperatureIndex	TemperatureIndex 抗张强度	IEC 60216	155
Melting temperature	Melting temperature	ISO 11357-3	225to250 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ISO 11359-2	3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to55°C	ISO 11359-2	6E-05 cm/cm/°C
thermal conductivity	thermal conductivity 23°C	ISO 8302	0.27 W/m/K
RTI Elec	RTI Elec	UL 746	140 °C
RTI Imp	RTI Imp	UL 746	125 °C
RTI Str	RTI Str	UL 746	140 °C
Half Interval	Half Interval --8	IEC 60216	13.5 °C
	Half Interval	Half Interval --9	IEC 60216	10.2 °C
	Half Interval	Half Interval	Half Interval --10	IEC 60216	10.2 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	220 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	200 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B120	205 °C
Ball Pressure Test	Ball Pressure Test 220°C	IEC 60695-10-2	Pass

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Apparent density	Apparent density	ISO 60	0.80 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 260°C/5.0kg	ISO 1133	30.0 cm3/10min
Shrinkage rate	Shrinkage rate TD:270°C,2.00mm2	ISO 294-4	0.90 %
	Shrinkage rate	Shrinkage rate TD:120°C,2hr,2.00mm3	ISO 294-4	0.20 %
		Shrinkage rate	Shrinkage rate MD:270°C,2.00mm2	ISO 294-4	0.30 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD:120°C,2hr,2.00mm3	ISO 294-4	0.10 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.30 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.10 %
Viscosity value	Viscosity value 降低的粘度	ISO 1628	91.0 ml/g

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dielectric strength	Dielectric strength 23°C,1.00mm	IEC 60243-1	27 KV/mm
Relative permittivity	Relative permittivity 23°C,100Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	Relative permittivity 23°C,1MHz	IEC 60250	3.80
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 2

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	200 Mpa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

ISO 2039-1

200 Mpa

film	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Thin film puncture strength	Thin film puncture strength	ISO 6603-2	2.10 J
Thin film puncture strength	Thin film puncture strength	ISO 6603-2	650 N

film

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Thin film puncture strength

ISO 6603-2

2.10 J

Thin film puncture strength

ISO 6603-2

650 N

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Electrolytic corrosion	Electrolytic corrosion	IEC 60426	A1
ISO Shortcut	ISO Shortcut	ISO 7792	PBT+PET.GHLMR.09-100.GF30

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Electrolytic corrosion

IEC 60426

ISO Shortcut

ISO 7792

PBT+PET.GHLMR.09-100.GF30

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.