So sánh vật liệu
Thông số kỹ thuật
impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | COVESTRO GERMANY/T7331 |
---|---|---|---|
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 55 kJ/m² |
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 65 kJ/m² |
Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 55 kJ/m² |
flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | COVESTRO GERMANY/T7331 |
---|---|---|---|
Extreme Oxygen Index | ISO 4589-2 | 21 % | |
Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 750 °C |
UL flame retardant rating | 0.8mm | UL 94 | HB |
1.6mm | UL 94 | HB |
mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | COVESTRO GERMANY/T7331 |
---|---|---|---|
Bending strain | 23°C | 3.0 % | |
Tensile modulus | 23°C | ASTM D638 | 9980 Mpa |
Bending modulus | 23°C | ISO 178/A | 10300 Mpa |
tensile strength | Break,23°C | ISO 527-2/5 | 145 Mpa |
Break,23°C | ASTM D638 | 123 Mpa | |
Tensile strain | Break,23°C | ISO 527-2/5 | 2.8 % |
bending strength | 23°C | ASTM D790 | 207 Mpa |
23°C | ISO 178 | 230 Mpa | |
Tensile creep modulus | 1hr | ISO 899-1 | 10000 Mpa |
Tensile modulus | 23°C | ISO 527-2/1 | 10400 Mpa |
elongation | Break,23°C | ASTM D638 | 2.5 % |
Tensile creep modulus | 1000hr | ISO 899-1 | 8500 Mpa |
Bending modulus | 23°C | ASTM D790 | 8550 Mpa |
thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | COVESTRO GERMANY/T7331 |
---|---|---|---|
RTI Elec | UL 746 | 140 °C | |
Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 220 °C |
1.8MPa,Unannealed | ISO 75-2/A | 200 °C | |
Linear coefficient of thermal expansion | TD:23to55°C | ISO 11359-2 | 6E-05 cm/cm/°C |
TemperatureIndex | 抗张强度 | IEC 60216 | 155 |
Half Interval | --8 | IEC 60216 | 13.5 °C |
Vicat softening temperature | ISO 306/B120 | 205 °C | |
Half Interval | --9 | IEC 60216 | 10.2 °C |
TemperatureIndex | 拉伸冲击强度 | IEC 60216 | 140 |
thermal conductivity | 23°C | ISO 8302 | 0.27 W/m/K |
RTI Str | UL 746 | 140 °C | |
Linear coefficient of thermal expansion | MD:23to55°C | ISO 11359-2 | 3E-05 cm/cm/°C |
Ball Pressure Test | 220°C | IEC 60695-10-2 | Pass |
Melting temperature | ISO 11357-3 | 225to250 °C | |
RTI Imp | UL 746 | 125 °C | |
TemperatureIndex | 介电强度 | IEC 60216 | 155 |
Half Interval | --10 | IEC 60216 | 10.2 °C |
Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | COVESTRO GERMANY/T7331 |
---|---|---|---|
Apparent density | ISO 60 | 0.80 g/cm³ | |
Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | 0.10 % |
Melt Volume Flow Rate (MVR) | 260°C/5.0kg | ISO 1133 | 30.0 cm3/10min |
Shrinkage rate | TD:270°C,2.00mm2 | ISO 294-4 | 0.90 % |
TD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.20 % | |
Viscosity value | 降低的粘度 | ISO 1628 | 91.0 ml/g |
Shrinkage rate | MD:120°C,2hr,2.00mm3 | ISO 294-4 | 0.10 % |
Water absorption rate | Saturation,23°C | ISO 62 | 0.30 % |
Shrinkage rate | MD:270°C,2.00mm2 | ISO 294-4 | 0.30 % |
Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | COVESTRO GERMANY/T7331 |
---|---|---|---|
Dielectric strength | 23°C,1.00mm | IEC 60243-1 | 27 KV/mm |
Relative permittivity | 23°C,1MHz | IEC 60250 | 3.80 |
23°C,100Hz | IEC 60250 | 4.00 | |
Compared to the anti leakage trace index | SolutionA | IEC 60112 | PLC 2 |
hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | COVESTRO GERMANY/T7331 |
---|---|---|---|
Ball Pressure Test | ISO 2039-1 | 200 Mpa |
film | Điều kiện kiểm tra | Phương pháp kiểm tra | COVESTRO GERMANY/T7331 |
---|---|---|---|
Thin film puncture strength | ISO 6603-2 | 650 N | |
ISO 6603-2 | 2.10 J |
Supplementary Information | Điều kiện kiểm tra | Phương pháp kiểm tra | COVESTRO GERMANY/T7331 |
---|---|---|---|
Electrolytic corrosion | IEC 60426 | A1 | |
ISO Shortcut | ISO 7792 | PBT+PET.GHLMR.09-100.GF30 |