PBT+ASA Ultradur® S 4090 G4 BK05110 BASF GERMANY

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	7.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179	43 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	55 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180	7.0 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile strain	Tensile strain Break,-40°C	ISO 527-2	2.7 %
Tensile modulus	Tensile modulus 23°C	ISO 527-2	6900 MPa
tensile strength	tensile strength Break,-40°C	ISO 527-2	160 MPa
	tensile strength	tensile strength Break,23°C	ISO 527-2	100 MPa
		tensile strength	tensile strength Break,80°C	ISO 527-2	68.0 MPa
		tensile strength	tensile strength	tensile strength Break,120°C	ISO 527-2	42.0 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2	2.5 %
	Tensile strain	Tensile strain Break,80°C	ISO 527-2	4.2 %
		Tensile strain	Tensile strain Break,120°C	ISO 527-2	7.4 %
		Tensile strain	Tensile strain	Tensile strain Break,150°C	ISO 527-2	6.7 %
Bending modulus	Bending modulus 23°C	ISO 178	6400 MPa
tensile strength	tensile strength Break,150°C	ISO 527-2	32.2 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	205 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	160 °C
Melting temperature	Melting temperature	ISO 3146	223 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD		4E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD	ISO 294-4	0.74 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.43 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.40 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.20 %
density	density	ISO 1183	1.39 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 275°C/2.16kg	ISO 1133	20.0 cm³/10min

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	1E+14 ohms
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm
Dielectric constant	Dielectric constant 100Hz	IEC 60250	3.70
Dielectric constant	Dielectric constant	Dielectric constant 1MHz	IEC 60250	3.60
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 1
Dissipation factor	Dissipation factor 100Hz	IEC 60250	3E-03
Dissipation factor	Dissipation factor	Dissipation factor 1MHz	IEC 60250	0.019

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.