| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179/1eA | 5.0 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | 45 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | 45 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180/1A | 7.0 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/1A | 8.0 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength -30°C | ISO 180/1U | 45 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ISO 180/1U | 45 kJ/m² |
| Dart impact | Dart impact 23°C,TotalEnergy | ASTM D3763 | 8.00 J |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| tensile strength | tensile strength Yield | ISO 527-2/5 | 125 Mpa |
| tensile strength | tensile strength Yield | ASTM D638 | 120 Mpa |
| Tensile modulus | Tensile modulus | ISO 527-2/1 | 9300 Mpa |
| Tensile modulus | Tensile modulus | ASTM D638 | 9300 Mpa |
| tensile strength | tensile strength Break | ASTM D638 | 120 Mpa |
| tensile strength | tensile strength Break | ISO 527-2/5 | 125 Mpa |
| Tensile strain | Tensile strain Yield | ASTM D638 | 3.0 % |
| Tensile strain | Tensile strain Yield | ISO 527-2/5 | 2.0 % |
| Tensile strain | Tensile strain Break | ASTM D638 | 3.0 % |
| Bending modulus | Bending modulus 50.0mmSpan | ASTM D790 | 7580 Mpa |
| Bending modulus | Bending modulus | ISO 178 | 8500 Mpa |
| bending strength | bending strength | ISO 178 | 195 Mpa |
| Tensile strain | Tensile strain Break | ISO 527-2/5 | 2.0 % |
| bending strength | bending strength Break,50.0mmSpan | ASTM D790 | 189 Mpa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：-40to40°C | ASTME831 | 2.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：-40to40°C | ISO 11359-2 | 2.5E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：-40to40°C | ASTME831 | 1.2E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：-40to40°C | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B120 | 215 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 215 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,3.20mm | ASTM D648 | 203 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 204 °C |
| Vicat softening temperature | Vicat softening temperature | ASTM D152514 | 215 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/A50 | 223 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed,3.20mm | ASTM D648 | 220 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed,6.40mm | ASTM D648 | 216 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 217 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Shrinkage rate | Shrinkage rate TD：--5 | Internal Method | 0.60-0.90 % |
| Shrinkage rate | Shrinkage rate MD：3.20mm | Internal Method | 0.30-0.80 % |
| Shrinkage rate | Shrinkage rate MD：--4 | Internal Method | 0.30-0.70 % |
| Shrinkage rate | Shrinkage rate MD：--3 | Internal Method | 0.30-0.50 % |
| Shrinkage rate | Shrinkage rate MD：--2 | Internal Method | 0.50-0.80 % |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 0.080 % |
| Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 0.26 % |
| Water absorption rate | Water absorption rate 24hr | ASTM D570 | 0.060 % |
| Shrinkage rate | Shrinkage rate TD：3.20mm | Internal Method | 0.50-1.0 % |
| Shrinkage rate | Shrinkage rate TD：--4 | Internal Method | 0.50-1.0 % |
| Shrinkage rate | Shrinkage rate TD：--3 | Internal Method | 0.40-0.60 % |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 250°C/2.16kg | ISO 1133 | 13.0 cm3/10min |
| melt mass-flow rate | melt mass-flow rate 250°C/2.16kg | ASTM D1238 | 17 g/10min |
| Specific volume | Specific volume | ASTM D792 | 0.650 cm³/g |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Volume resistivity | Volume resistivity | ASTM D257 | >3.2E+16 ohms·cm |
| Dielectric strength | Dielectric strength 1.60mm,in Oil | ASTM D149 | 25 KV/mm |
| Dissipation factor | Dissipation factor 1MHz | ASTM D150 | 0.020 |
| Dissipation factor | Dissipation factor 100Hz | ASTM D150 | 2E-03 |
| Dielectric constant | Dielectric constant 1MHz | ASTM D150 | 3.70 |
| Dielectric strength | Dielectric strength 3.20mm,inAir | ASTM D149 | 19 KV/mm |
| Dielectric constant | Dielectric constant 100Hz | ASTM D150 | 3.80 |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Rockwell hardness | Rockwell hardness R-Scale | ASTM D785 | 118 |
| Supplementary Information | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Filling material | Filling material | ASTM D229 | 30 % |