PBT/F/PTFE LNP™ LUBRICOMP™ WFL-4036 NAT SABIC INNOVATIVE US

213

Đặc tính:
Chịu nhiệt độ caoChống lão hóa
Lĩnh vực ứng dụng:
Phụ tùng ô tôLĩnh vực điện
So sánh Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	ISO 6603-2	2.61 J
Dart impact	Dart impact 23°C,EnergyatPeakLoad	ASTM D3763	13.7 J
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	43 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	9.2 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Wear factor	Wear factor Washer	ASTM D3702Modified	42.0 10^-10in^5-min/ft-lb-hr
Friction coefficient	Friction coefficient Static	ASTM D3702Modified	0.41
Friction coefficient	Friction coefficient	Friction coefficient Dynamic	ASTM D3702Modified	0.57
Tensile strain	Tensile strain Break	ISO 527-2	2.2 %
elongation	elongation Break	ASTM D638	2.3 %
tensile strength	tensile strength Break	ISO 527-2	118 Mpa
tensile strength	tensile strength	tensile strength Break	ASTM D638	118 Mpa
Tensile modulus	Tensile modulus	ISO 527-2/1	10600 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ASTM D638	10300 Mpa
bending strength	bending strength	ISO 178	187 Mpa
bending strength	bending strength	bending strength	ASTM D790	193 Mpa
Bending modulus	Bending modulus	ISO 178	10000 Mpa
Bending modulus	Bending modulus	Bending modulus	ASTM D790	10200 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	214 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	3.9E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	3.9E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	218 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	6.7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	6.7E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate MD:24hr	ISO 294-4	0.10-0.30 %
	Shrinkage rate	Shrinkage rate TD:24hr	ISO 294-4	0.50-1.0 %
		Shrinkage rate	Shrinkage rate TD：24hr	ASTM D955	0.50-1.0 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD：24hr	ASTM D955	0.10-0.30 %
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.040 %
Water absorption rate	Water absorption rate	Water absorption rate 24hr,50%RH	ASTM D570	0.040 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.