flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating 2.0mm	UL 94	5VB
		UL flame retardant rating	UL flame retardant rating 0.70mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 1.2mm	UL 94	V-1

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1	2600 Mpa
tensile strength	tensile strength Yield	ISO 527-2/50	63.0 Mpa
tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	48.0 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2/50	3.0 %
Tensile strain	Tensile strain	Tensile strain Break	ISO 527-2/50	80 %
Bending modulus	Bending modulus	ISO 178	2600 Mpa
bending strength	bending strength	ISO 178	95.0 Mpa
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 没Notched	ISO 179	NB KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 带Notched	ISO 179	15 KJ/m
Tensile modulus	Tensile modulus	ISO 527-1	2600 Mpa
Tensile stress	Tensile stress	ISO 527-1	63 Mpa
Tensile stress	Tensile stress	Tensile stress Break	ISO 527-1	48 Mpa
elongation at yield	elongation at yield	ISO 527-1	3 %
Elongation at Break	Elongation at Break	ISO 527-1	80 %
Bending modulus	Bending modulus	ISO 178	2600 Mpa
bending strength	bending strength	ISO 178	95 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	94.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	84.0 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	97.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	8E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.80MPa	ISO 75-1	84 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45Mpa	ISO 75-2	94 °C
Vicat softening temperature	Vicat softening temperature	ISO 306	97 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ISO 11359-2	0.8
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow	ISO 11359-2	0.8
UL flame retardant rating	UL flame retardant rating	UL 94	V-0

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD:4.00mm	Internal Method	0.50-0.70 %
	Shrinkage rate	Shrinkage rate MD:4.00mm	Internal Method	0.50-0.70 %
		Shrinkage rate	Shrinkage rate Flow		0.5-0.7 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate Across Flow		0.5-0.7 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	1E+16 ohms

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Surface resistivity

IEC 60093

1E+16 ohms

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.