mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	TEIJIN JAPAN/TN-7000
Elongation at Break		ISO 527-1	80 %
Impact strength of cantilever beam gap	带Notched	ISO 179	15 KJ/m
tensile strength	Yield	ISO 527-2/50	63.0 Mpa
bending strength		ISO 178	95 Mpa
Tensile strain	Break	ISO 527-2/50	80 %
tensile strength	Break	ISO 527-2/50	48.0 Mpa
Tensile stress	Break	ISO 527-1	48 Mpa
Tensile stress			ISO 527-1	63 Mpa
elongation at yield		ISO 527-1	3 %
Impact strength of cantilever beam gap	没Notched	ISO 179	NB KJ/m
Tensile modulus		ISO 527-2/1	2600 Mpa
Tensile modulus			ISO 527-1	2600 Mpa
Bending modulus		ISO 178	2600 Mpa
Tensile strain	Yield	ISO 527-2/50	3.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	TEIJIN JAPAN/TN-7000
Hot deformation temperature	1.80MPa	ISO 75-1	84 °C
		0.45MPa,Unannealed	ISO 75-2/B	94.0 °C
		1.8MPa,Unannealed	ISO 75-2/A	84.0 °C
		0.45Mpa	ISO 75-2	94 °C
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	0.8
Linear coefficient of thermal expansion		TD	ISO 11359-2	8E-05 cm/cm/°C
Vicat softening temperature		ISO 306	97 °C
Vicat softening temperature			ISO 306/B50	97.0 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	0.8
Linear coefficient of thermal expansion		MD	ISO 11359-2	8E-05 cm/cm/°C
UL flame retardant rating		UL 94	V-0

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	TEIJIN JAPAN/TN-7000
Shrinkage rate	MD:4.00mm	Internal Method	0.50-0.70 %
		TD:4.00mm	Internal Method	0.50-0.70 %
		Flow		0.5-0.7 %
		Across Flow		0.5-0.7 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	TEIJIN JAPAN/TN-7000
Surface resistivity		IEC 60093	1E+16 ohms