PLA Generic PLA Generic

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	1.4to5.5 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	8.5to24 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	16to47 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180	3.4to6.4 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Break,23°C	ISO 527-2	1.0to12 %
Bending modulus	Bending modulus 23°C	ASTM D790	2390to4930 MPa
Bending modulus	Bending modulus	Bending modulus 23°C	ISO 178	305to9500 MPa
bending strength	bending strength 23°C	ASTM D790	47.9to110 MPa
bending strength	bending strength	bending strength 23°C	ISO 178	9.00to111 MPa
tensile strength	tensile strength Break,23°C	ISO 527-2	13.8to70.0 MPa
tensile strength	tensile strength	tensile strength 23°C	ASTM D638	47.8to68.9 MPa
elongation	elongation Yield,23°C	ASTM D638	9.8to10 %
	elongation	elongation Yield,23°C	ISO 527-2	1.0to8.5 %
	elongation	elongation	elongation Break,23°C	ASTM D638	0.50to9.2 %
Tensile modulus	Tensile modulus 23°C	ASTM D638	2020to3540 MPa
Tensile modulus	Tensile modulus	Tensile modulus 23°C	ISO 527-2	310to5620 MPa
tensile strength	tensile strength Yield,23°C	ASTM D638	61.0to65.5 MPa
	tensile strength	tensile strength Yield,23°C	ISO 527-2	15.5to72.0 MPa
	tensile strength	tensile strength	tensile strength Break,23°C	ASTM D638	48.8to56.2 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	49.7to52.3 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	50.0to120 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	48.0to50.2 °C
Glass transition temperature	Glass transition temperature --	ASTME1356	56.4to57.5 °C
Glass transition temperature	Glass transition temperature	Glass transition temperature --	DSC	43.8to62.5 °C
Vicat softening temperature	Vicat softening temperature	ISO 306	54.7to63.5 °C
Melting temperature	Melting temperature		157to170 °C
Crystallization peak temperature	Crystallization peak temperature DSC	ASTM D3418	130to164 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 210°C/2.16kg	ASTM D1238	6.0to78 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 190°C/2.16kg	ISO 1133	1.5to36 g/10min
Shrinkage rate	Shrinkage rate MD:23°C	ASTM D955	0.37to0.41 %
Shrinkage rate	Shrinkage rate	Shrinkage rate 23°C	ISO 294-4	0.30to1.1 %
density	density --	ASTM D792	1.23to1.24 g/cm³
density	density	density 23°C	ISO 1183	1.24to1.26 g/cm³

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.