PBT LNP™ THERMOTUF™ WF008N compound SABIC
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ASTM D256 | 140 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C7 | ISO 180/1A | 13 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C7 | ISO 180/1A | 14 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ASTM D4812 | 1100 J/m |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C7 | ISO 180/1U | 69 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179/2C | 13 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/2C | 14 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/2U | 85 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ASTM D256 | 130 J/m |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| tensile strength | tensile strength Break3 | ASTM D638 | 126 MPa |
| tensile strength | tensile strength Break | ISO 527-2/5 | 131 MPa |
| elongation | elongation Yield3 | ASTM D638 | 3.0 % |
| elongation | elongation Yield | ISO 527-2/5 | 2.9 % |
| elongation | elongation Break3 | ASTM D638 | 3.0 % |
| Tensile modulus | Tensile modulus --2 | ASTM D638 | 10600 MPa |
| Tensile modulus | Tensile modulus -- | ISO 527-2/1 | 11000 MPa |
| tensile strength | tensile strength Yield3 | ASTM D638 | 126 MPa |
| tensile strength | tensile strength Yield | ISO 527-2/5 | 131 MPa |
| elongation | elongation Break | ISO 527-2/5 | 2.9 % |
| Bending modulus | Bending modulus 50.0mmSpan4 | ASTM D790 | 9200 MPa |
| Bending modulus | Bending modulus --5 | ISO 178 | 9700 MPa |
| bending strength | bending strength --5,6 | ISO 178 | 208 MPa |
| bending strength | bending strength Break,50.0mmSpan4 | ASTM D790 | 194 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,3.20mm | ASTM D648 | 207 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,6.40mm | ASTM D648 | 209 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan8 | ISO 75-2/Af | 203 °C |
| Vicat softening temperature | Vicat softening temperature -- | ASTM D15259 | 205 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 203 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD:-40to40°C | ASTME831 | 1E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD:23to80°C | ASTME831 | 1.4E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD:-40to40°C | ISO 11359-2 | 1.8E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD:23to80°C | ISO 11359-2 | 1.1E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD:-40to40°C | ASTME831 | 8.9E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD:23to80°C | ASTME831 | 1.2E-04 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD:-40to40°C | ISO 11359-2 | 9.2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD:23to80°C | ISO 11359-2 | 1.5E-04 cm/cm/°C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| density | density | ASTM D792 | 1.61 g/cm³ |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 250°C/5.0kg | ISO 1133 | 7.00 cm³/10min |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 275°C/5.0kg | ISO 1133 | 11.0 cm³/10min |
| Shrinkage rate | Shrinkage rate MD | Internal Method | 0.27 % |
| Shrinkage rate | Shrinkage rate TD | Internal Method | 0.80 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Volume resistivity | Volume resistivity | ASTM D257 | 2.2E+15 ohms·cm |
| Dielectric constant | Dielectric constant 1.10GHz | Internal Method | 3.65 |
| Dielectric constant | Dielectric constant 1.90GHz | Internal Method | 3.72 |
| Dissipation factor | Dissipation factor 1.10GHz | Internal Method | 0.013 |
| Dissipation factor | Dissipation factor 1.90GHz | Internal Method | 0.012 |