PBT LNP™ THERMOTUF™ WF008N compound SABIC
--
--
--
- -
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Thông số kỹ thuật

impact performanceĐiều kiện kiểm traPhương pháp kiểm traSABIC/LNP™ THERMOTUF™ WF008N compound
Impact strength of cantilever beam gap23°C7ISO 180/1A14 kJ/m²
Charpy Notched Impact Strength23°CISO 179/2C14 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/2U85 kJ/m²
Impact strength of cantilever beam gap-30°C7ISO 180/1A13 kJ/m²
Suspended wall beam without notch impact strength23°CASTM D48121100 J/m
Impact strength of cantilever beam gap23°CASTM D256140 J/m
Charpy Notched Impact Strength-30°CISO 179/2C13 kJ/m²
Suspended wall beam without notch impact strength23°C7ISO 180/1U69 kJ/m²
Impact strength of cantilever beam gap-30°CASTM D256130 J/m
mechanical propertiesĐiều kiện kiểm traPhương pháp kiểm traSABIC/LNP™ THERMOTUF™ WF008N compound
elongationBreakISO 527-2/52.9 %
Bending modulus--5ISO 1789700 MPa
50.0mmSpan4ASTM D7909200 MPa
Tensile modulus--2ASTM D63810600 MPa
elongationYield3ASTM D6383.0 %
Tensile modulus--ISO 527-2/111000 MPa
tensile strengthYieldISO 527-2/5131 MPa
elongationYieldISO 527-2/52.9 %
Break3ASTM D6383.0 %
bending strengthBreak,50.0mmSpan4ASTM D790194 MPa
tensile strengthBreak3ASTM D638126 MPa
BreakISO 527-2/5131 MPa
Yield3ASTM D638126 MPa
bending strength--5,6ISO 178208 MPa
thermal performanceĐiều kiện kiểm traPhương pháp kiểm traSABIC/LNP™ THERMOTUF™ WF008N compound
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648207 °C
Vicat softening temperature--ISO 306/B50203 °C
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D648209 °C
Linear coefficient of thermal expansionTD:23to80°CASTME8311.2E-04 cm/cm/°C
MD:-40to40°CASTME8311E-05 cm/cm/°C
TD:-40to40°CISO 11359-29.2E-05 cm/cm/°C
TD:-40to40°CASTME8318.9E-05 cm/cm/°C
Vicat softening temperature--ASTM D15259205 °C
Linear coefficient of thermal expansionMD:23to80°CASTME8311.4E-05 cm/cm/°C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpan8ISO 75-2/Af203 °C
Linear coefficient of thermal expansionMD:23to80°CISO 11359-21.1E-05 cm/cm/°C
MD:-40to40°CISO 11359-21.8E-05 cm/cm/°C
TD:23to80°CISO 11359-21.5E-04 cm/cm/°C
Physical propertiesĐiều kiện kiểm traPhương pháp kiểm traSABIC/LNP™ THERMOTUF™ WF008N compound
Melt Volume Flow Rate (MVR)275°C/5.0kgISO 113311.0 cm³/10min
Shrinkage rateMDInternal Method0.27 %
densityASTM D7921.61 g/cm³
Melt Volume Flow Rate (MVR)250°C/5.0kgISO 11337.00 cm³/10min
Shrinkage rateTDInternal Method0.80 %
Electrical performanceĐiều kiện kiểm traPhương pháp kiểm traSABIC/LNP™ THERMOTUF™ WF008N compound
Volume resistivityASTM D2572.2E+15 ohms·cm
Dielectric constant1.10GHzInternal Method3.65
Dissipation factor1.90GHzInternal Method0.012
Dielectric constant1.90GHzInternal Method3.72
Dissipation factor1.10GHzInternal Method0.013