ABS M205FC ELIX POLYMERS SPANISH
So sánhBảng thông số kỹ thuật
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Burning wire flammability index | Burning wire flammability index 2.00 mm | IEC 60695-2-12 | 650 ℃ |
| UL flame retardant rating | UL flame retardant rating 1.60 mm | UL 94 | HB mm/min |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| bending strength | bending strength 23℃ | ISO 178 | 75.0 MPa |
| Bending modulus | Bending modulus 23℃ | ISO 178 | 2600 MPa |
| Elongation at Break | Elongation at Break 23℃ | ISO 527-2/50 | 20 % |
| Tensile strain | Tensile strain Break,23℃ | ISO 527-2/50 | ＞15 % |
| Tensile strain | Tensile strain Yield, 23℃ | ISO 527-2/50 | 2.6 % |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30℃ | ISO 179/1eA | 7.0 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23℃ | ISO 179/1eA | 16 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30℃ | ISO 179/1eU | 100 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23℃ | ISO 179/1eU | 120 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30℃ | ISO 180/1A | 7.0 kJ/m² |
| tensile strength | tensile strength Yield, 23℃ | ISO 527-2/50 | 50.5 MPa |
| tensile strength | tensile strength Break, 23℃ | ISO 527-2/50 | 36.5 |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23℃ | ISO 180/1A | 15 kJ/m² |
| Tensile modulus | Tensile modulus 23℃ | ISO 527-2/1 | 2550 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion 23 to 55℃，Across Flow | ISO 11359-2 | 0.000081 |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion 23 to 55℃ | ISO 11359-2 | 0.000078 cm/cm/℃ |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B120 | 101 ℃ |
| Vicat softening temperature | Vicat softening temperature | ISO 306/B50 | 98.0 ℃ |
| Hot deformation temperature | Hot deformation temperature 1.8 MPa, Unannealed | ISO 75-2/A | 94.0 ℃ |
| Hot deformation temperature | Hot deformation temperature 0.45 MPa, Unannealed | ISO 75-2/B | 98.0 ℃ |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Shore hardness | Shore hardness 球压硬度 | ISO 2039-1 | 106 MPa |
| Shrinkage rate | Shrinkage rate MD | ISO 294-4 | 0.50 % |
| Shrinkage rate | Shrinkage rate TD | ISO 294-4 | 0.50 % |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 220℃/10.0 kg | ISO 1133 | 20.0 cm³/10min |
| density | density | ISO 1183 | 1.06 g/cm³ |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Dissipation factor | Dissipation factor 23℃, 1 MHz | IEC 60250 | 0.0096 |
| Dissipation factor | Dissipation factor 23℃, 100 Hz | IEC 60250 | 0.0053 |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index Solution A | IEC 60112 | PLC 0 |
| Relative permittivity | Relative permittivity 23℃, 1 MHz | IEC 60250 | 2.82 |
| Volume resistivity | Volume resistivity | IEC 60093 | 2E+16 ohm·cm |
| Surface resistivity | Surface resistivity | IEC 60093 | 2E+17 ohm |
| Relative permittivity | Relative permittivity 23℃, 100 Hz | IEC 60250 | 3.04 |