PBT VESTODUR® GF20 Altuglas International of Arkema Inc.

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C,Complete Break	ISO 179/1eA	8.5 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C,Complete Break	ISO 179/1eA	9.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C,Complete Break	ISO 179/1eU	65 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C,Complete Break	ISO 179/1eU	60 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot filament ignition temperature	Hot filament ignition temperature 2.0mm	IEC 60695-2-13	800 °C
Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	750 °C
Flammability level	Flammability level 1.6mm	IEC 60695-11-10,-20	HB
Flammability level	Flammability level	Flammability level 0.8mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	20 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength	ISO 527-2/50	140 MPa
Tensile strain	Tensile strain Break	ISO 527-2/50	3.5 %
Tensile modulus	Tensile modulus	ISO 527-2	7200 MPa

mechanical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

tensile strength

ISO 527-2/50

140 MPa

Tensile strain

Break

ISO 527-2/50

3.5 %

Tensile modulus

ISO 527-2

7200 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:23to55°C	ISO 11359-2	7E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	220 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	195 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A	220 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B	210 °C
Melting temperature	Melting temperature	ISO 11357-3	221to226 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:23to55°C	ISO 11359-2	6E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.45 %
Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.30 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ISO 294-4	1.5 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 250°C/2.16kg	ISO 1133	16.0 cm³/10min
density	density 23°C	ISO 1183	1.47 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 2
Compared to the anti leakage trace index	Compared to the anti leakage trace index	Compared to the anti leakage trace index --4	IEC 60112	PLC 2
Dissipation factor	Dissipation factor 23°C,1MHz	IEC 60250	0.018
Dissipation factor	Dissipation factor	Dissipation factor 23°C,100Hz	IEC 60250	3E-03
Relative permittivity	Relative permittivity 23°C,1MHz	IEC 60250	4.20
Relative permittivity	Relative permittivity	Relative permittivity 23°C,100Hz	IEC 60250	3.80
Dielectric strength	Dielectric strength 1.00mm,in Oil	IEC 60243-1	27 kV/mm
Volume resistivity	Volume resistivity 23°C	IEC 60093	1E+15 ohms·cm
Surface resistivity	Surface resistivity	IEC 60093	1E+13 ohms

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	190 MPa
Shore hardness	Shore hardness ShoreD	ISO 868	82

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

ISO 2039-1

190 MPa

Shore hardness

ShoreD

ISO 868

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Electrolytic corrosion	Electrolytic corrosion	IEC 60426	A1step

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Electrolytic corrosion

IEC 60426

A1step

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.