film	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation MD:Break,38μm,Blown Film	ASTM D882	660 %
tensile strength	tensile strength TD:Break,38μm,Blown Film	ASTM D882	25.0 MPa
tensile strength	tensile strength	tensile strength MD:Break,38μm,Blown Film	ASTM D882	30.0 MPa
Elmendorf tear strength	Elmendorf tear strength TD:38μm,Blown Film	ASTM D1922	390 g
Elmendorf tear strength	Elmendorf tear strength	Elmendorf tear strength MD:38μm,Blown Film	ASTM D1922	200 g
Dart impact	Dart impact 38μm,Blown Film	ASTM D1709A	140 g
elongation	elongation TD:Break,38μm,Blown Film	ASTM D882	730 %
Secant modulus	Secant modulus 1%Secant,TD:38μm,Blown Film	ASTM D882	230 MPa
Secant modulus	Secant modulus	Secant modulus 1%Secant,MD:38μm,Blown Film	ASTM D882	190 MPa
film thickness	film thickness		38 µm
tensile strength	tensile strength TD:Yield,38μm,Blown Film	ASTM D882	10.0 MPa
tensile strength	tensile strength	tensile strength MD:Yield,38μm,Blown Film	ASTM D882	10.0 MPa

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Low friction puncture	Low friction puncture 38.0μm	Internal Method	320 J/cm

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Low friction puncture

38.0μm

Internal Method

320 J/cm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.