| Burning wire flammability index | Burning wire flammability index 3.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 1.5mm | IEC 60695-2-13 | 750 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 3.0mm | IEC 60695-2-13 | 750 °C |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index | IEC 60112 | PLC 3 |
| RTI Str | RTI Str 1.5mm | UL 746 | 60.060.0 °C |
| RTI Imp | RTI Imp 3.0mm | UL 746 | 60.0 °C |
| RTI Imp | RTI Imp 1.5mm | UL 746 | 60.0 °C |
| RTI Elec | RTI Elec 3.0mm | UL 746 | 60.0 °C |
| RTI Elec | RTI Elec 1.5mm | UL 746 | 60.0 °C |
| Ball Pressure Test | Ball Pressure Test 125°C | IEC 60695-10-2 | Pass |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 156 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/A50 | 190 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed | ISO 75-2/Af | 60.0 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed | ISO 75-2/Bf | 113 °C |
| Extreme Oxygen Index | Extreme Oxygen Index | ISO 4589-2 | 31 % |
| Burning rate | Burning rate 3.00mm,自动灭火 | ISO 3795 | 0.0 mm/min |
| Burning rate | Burning rate 1.50mm,自动灭火 | ISO 3795 | 0.0 mm/min |
| Tensile modulus | Tensile modulus | ISO 527-2/1A/1 | 2500 MPa |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 250°C/5.0kg | ISO 1133 | 12.0 cm³/10min |
| density | density | ISO 1183/A | 1.30 g/cm³ |
| Burning wire flammability index | Burning wire flammability index 1.5mm | IEC 60695-2-12 | 960 °C |
| Burning wire flammability index | Burning wire flammability index 0.75mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | UL flame retardant rating 2.0mm | IEC 60695-11-10,-20 | 5VA |
| UL flame retardant rating | UL flame retardant rating 3.0mm | IEC 60695-11-10,-20 | V-0 |
| UL flame retardant rating | UL flame retardant rating 1.5mm | IEC 60695-11-10,-20 | V-0 |
| UL flame retardant rating | UL flame retardant rating 2.0mm | UL 94 | 5VA |
| UL flame retardant rating | UL flame retardant rating 3.0mm | UL 94 | V-0 |
| UL flame retardant rating | UL flame retardant rating 1.5mm | UL 94 | V-0 |
| tensile strength | tensile strength Yield | ISO 527-2/1A/50 | 52.0 MPa |
| Tensile strain | Tensile strain Yield | ISO 527-2/1A/50 | 3.0 % |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179/1eA | 9.0 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 12 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | NoBreak |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | NoBreak |