PC LEXAN™ EXL1414-GY7D493 SABIC INNOVATIVE KOREA

146

Đặc tính:
Dễ dàng xử lý
Thanh khoản trung bình
Độ dẻo
Đồng trùng hợp
Hiệu suất phát hành tốt
Lĩnh vực ứng dụng:
phổ quát
Lĩnh vực điện
Lĩnh vực điện tử
So sánh
Xem giá

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dart impact	Dart impact 23°C, Total Energy	ASTM D3763	70.0 J
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	无断裂
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	770 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	870 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C8	ISO 180/1A	60 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C8	ISO 180/1A	70 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	70 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	65 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.40 mm	UL 94	HB
Burning wire flammability index	Burning wire flammability index 0.8 mm	IEC 60695-2-12	850 °C
Burning wire flammability index	Burning wire flammability index	Burning wire flammability index 1.0 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature 1.0 mm	IEC 60695-2-13	875 °C
Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 3.0 mm	IEC 60695-2-13	875 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength --5,6	ISO 178	85.0 Mpa
bending strength	bending strength	bending strength Yield, 50.0 mm Span4	ASTM D790	92.0 Mpa
Bending modulus	Bending modulus 50.0 mm Span4	ASTM D790	2230 Mpa
Bending modulus	Bending modulus	Bending modulus --5	ISO 178	2250 Mpa
elongation	elongation Break	ISO 527-2/50	120 %
	elongation	elongation Break3	ASTM D638	98 %
		elongation	elongation Yield	ISO 527-2/50	6.0 %
		elongation	elongation	elongation Yield3	ASTM D638	6.0 %
tensile strength	tensile strength Break	ISO 527-2/50	60.0 Mpa
	tensile strength	tensile strength Break3	ASTM D638	50.0 Mpa
		tensile strength	tensile strength Yield	ISO 527-2/50	57.0 Mpa
		tensile strength	tensile strength	tensile strength Yield3	ASTM D638	55.0 Mpa
Tensile modulus	Tensile modulus --	ISO 527-2/1	2150 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --2	ASTM D638	2020 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
Processing (melt) temperature	Processing (melt) temperature	295 to 315 °C
Spray nozzle temperature	Spray nozzle temperature	290 to 310 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	295 to 315 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	280 to 305 °C
Temperature at the rear of the barrel	Temperature at the rear of the barrel	270 to 295 °C
Suggested injection volume	Suggested injection volume	40 to 60 %
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
drying time	drying time	3.0 to 4.0 hr
drying temperature	drying temperature	120 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Mold temperature	Mold temperature	70 to 95 °C
Exhaust hole depth	Exhaust hole depth	0.025 to 0.076 mm
Screw speed	Screw speed	40 to 70 rpm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow : 23 to 80°C	ISO 11359-2	7.2E-5 cm/cm/°C
RTI Elec	RTI Elec	UL 746	130 °C
RTI Imp	RTI Imp	UL 746	120 °C
RTI	RTI	UL 746	125 °C
Ball Pressure Test	Ball Pressure Test 123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : -40 to 40°C	ASTM E831	7.0E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow : 23 to 80°C	ISO 11359-2	7.2E-5 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	146 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ASTM D152510	145 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Ae	128 °C
	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Be	140 °C
		Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	124 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 3.20 mm	ASTM D648	139 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density --	ISO 1183	1.19 g/cm³
density	density	density --	ASTM D792	1.18 g/cm³
Water absorption rate	Water absorption rate Saturation, 23°C	ISO 62	0.35 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	0.15 %
Shrinkage rate	Shrinkage rate Across FlowFlow : 3.20 mm	Internal Method	0.40 - 0.80 %
Shrinkage rate	Shrinkage rate	Shrinkage rate Flow : 3.20 mm	Internal Method	0.40 - 0.80 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/1.2 kg	ISO 1133	9.00 cm3/10min
melt mass-flow rate	melt mass-flow rate 300°C/1.2 kg	ASTM D1238	10 g/10 min

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dissipation factor	Dissipation factor 1 MHz	ASTM D150	9.3E-3
Dissipation factor	Dissipation factor	Dissipation factor 100 Hz	ASTM D150	1.2E-3
Dielectric constant	Dielectric constant 1 MHz	ASTM D150	2.64
Dielectric constant	Dielectric constant	Dielectric constant 100 Hz	ASTM D150	2.68
Volume resistivity	Volume resistivity	ASTM D257	> 1.0E+15 ohms·cm
Surface resistivity	Surface resistivity	ASTM D257	> 1.0E+15 ohms
Dielectric strength	Dielectric strength 0.800 mm, in Oil	ASTM D149	16 KV/mm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness L -Sale	ASTM D785	89
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	121

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

L -Sale

ASTM D785

Rockwell hardness

R-Scale

ASTM D785

121

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.