PEEK VESTAKEEP® Ultimate Altuglas International of Arkema Inc.

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C,Complete Break	ISO 179/1eA	9.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C,Complete Break	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C,Complete Break	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C,Complete Break	ISO 179/1eA	8.0 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 3.2mm	UL 94	V-0
Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature 2.0mm	IEC 60695-2-13	850 °C

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

3.2mm

UL 94

V-0

Burning wire flammability index

2.0mm

IEC 60695-2-12

960 °C

Hot filament ignition temperature

2.0mm

IEC 60695-2-13

850 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2	3400 MPa
tensile strength	tensile strength Yield	ISO 527-2	95.0 MPa
Tensile strain	Tensile strain Yield	ISO 527-2	5.0 %
Tensile strain	Tensile strain	Tensile strain Break	ISO 527-2	40 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ISO 306/A	335 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ISO 11359-2	6E-05 cm/cm/°C
Vicat softening temperature	Vicat softening temperature --	ISO 306/B	305 °C
Melting temperature	Melting temperature	ISO 11357-3	340 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.30 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 380°C/5.0kg	ISO 1133	7.00 cm³/10min
Shrinkage rate	Shrinkage rate TD:180°C,2.00mm	ISO 294-4	1.1 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD:180°C,2.00mm	ISO 294-4	0.90 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Relative permittivity	Relative permittivity 50Hz	IEC 60250	2.80
Relative permittivity	Relative permittivity	Relative permittivity 1MHz	IEC 60250	2.80
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA5	IEC 60112	PLC 3
Compared to the anti leakage trace index	Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 3
Surface resistivity	Surface resistivity	IEC 60093	1E+14 ohms
Volume resistivity	Volume resistivity	IEC 60093	1E+15 ohms·cm
Dielectric strength	Dielectric strength	IEC 60243-1	16 kV/mm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.