PA6 B3 GF 40 black (3383) AKRO-PLASTIC GmbH

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -40°C	ISO 179/1eA	14 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	14 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	18 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -40°C	ISO 179/1eU	110 kJ/m²
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	110 kJ/m²
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	110 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -40°C	ISO 180/1A	14 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	20 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Burning rate	Burning rate 1.00mm	FMVSS302	<100 mm/min
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Burning rate

1.00mm

FMVSS302

<100 mm/min

UL flame retardant rating

1.6mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1	12800 MPa
tensile strength	tensile strength Break	ISO 527-2/5	210 MPa
Tensile strain	Tensile strain Break	ISO 527-2/5	4.0 %
Bending modulus	Bending modulus	ISO 178	10300 MPa
bending strength	bending strength	ISO 178	300 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	215 °C
Melting temperature	Melting temperature	DIN EN11357-1	222 °C

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hot deformation temperature

1.8MPa,Unannealed

ISO 75-2/A

215 °C

Melting temperature

DIN EN11357-1

222 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density 23°C	ISO 1183	1.45 g/cm³
Spiral flow length	Spiral flow length	Internal Method	48.0 cm
Shrinkage rate	Shrinkage rate TD	ISO 294-4	0.80 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.30 %

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ReinforcementContent	ReinforcementContent	ISO 1172	40 %

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

ReinforcementContent

ISO 1172

40 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.