PPO(PPE) PREPERM® 255 Premix Oy

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -78°C	ISO 180	10 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -20°C	ISO 180	10 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180	20 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -78°C	ISO 180	无断裂
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength -20°C	ISO 180	无断裂
	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	无断裂

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 4.0mm	UL 94	V-1

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

4.0mm

UL 94

V-1

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield,4.00mm	ISO 527-2	65.0 MPa
tensile strength	tensile strength	tensile strength 4.00mm	ISO 527-2	45.0 MPa
Tensile strain	Tensile strain Yield,4.00mm	ISO 527-2	10 %
Tensile strain	Tensile strain	Tensile strain Break,4.00mm	ISO 527-2	40 %
Bending modulus	Bending modulus 4.00mm	ISO 178	2200 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/Bf	190 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/Af	167 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	210 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	160 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 300°C/2.16kg	ISO 1133	5.0 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 300°C/5.0kg	ISO 1133	15 g/10min
Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.90 %
density	density	ISO 1183	1.05 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dielectric constant	Dielectric constant 1.00GHz	Internal Method	2.55
Dissipation factor	Dissipation factor 1.00GHz	Internal Method	5E-04

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Dielectric constant

1.00GHz

Internal Method

2.55

Dissipation factor

1.00GHz

Internal Method

5E-04

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.