impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	8.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	200 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	850 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	8.0 kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -10°C	ISO 180/1A	8.0 kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	10 kJ/m²
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	70.0 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Break	ASTM D638	55.0 MPa
tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	60.0 MPa
elongation	elongation Yield	ASTM D638	6.0 %
Tensile strain	Tensile strain Yield	ISO 527-2/50	5.8 %
elongation	elongation Break	ASTM D638	92 %
Tensile strain	Tensile strain Break	ISO 527-2/50	120 %
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2220 MPa
Tensile modulus	Tensile modulus	ASTM D638	2370 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	2180 MPa
Bending modulus	Bending modulus	ISO 178	2000 MPa
bending strength	bending strength	ISO 178	89.0 MPa
bending strength	bending strength	bending strength Yield,50.0mmSpan	ASTM D790	94.0 MPa
tensile strength	tensile strength Yield	ASTM D638	57.0 MPa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2/50	60.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	116 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	104 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	102 °C
Vicat softening temperature	Vicat softening temperature	ASTM D152510	123 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	121 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	123 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to60°C	ISO 11359-2	6E-05 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	1E-04 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	1E-04 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to60°C	ISO 11359-2	7E-05 cm/cm/°C
thermal conductivity	thermal conductivity	ISO 8302	0.23 W/m/K

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.37 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.13 %
density	density	ASTM D792	1.20 g/cm³
density	density	density	ISO 1183	1.20 g/cm³
melt mass-flow rate	melt mass-flow rate 265°C/2.16kg	ASTM D1238	4.8 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 265°C/2.16kg	ISO 1133	3.80 cm³/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.50to0.80 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD：3.20mm	Internal Method	0.50to0.80 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.