PC+ABS Infino NH-1230U LOTTE KOREA

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	7.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	5.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.18mm	ASTM D256	69 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,6.35mm	ASTM D256	59 J/m

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.2mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	V-0

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.2mm

UL 94

V-0

UL flame retardant rating

3.0mm

UL 94

V-0

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus	ISO 178	550 MPa
bending strength	bending strength	ASTM D790	88.0 MPa
bending strength	bending strength	bending strength	ISO 178	90.0 MPa
Tensile modulus	Tensile modulus	ASTM D638	57.0 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/5	58.0 MPa
tensile strength	tensile strength Yield	ASTM D638	57.0 MPa
	tensile strength	tensile strength Yield	ISO 527-2/5	58.0 MPa
		tensile strength	tensile strength Break	ASTM D638	57.0 MPa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/5	58.0 MPa
elongation	elongation Break	ASTM D638	15 %
Tensile strain	Tensile strain Break	ISO 527-2/5	15 %
Bending modulus	Bending modulus	ASTM D790	5400 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	91.0 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,4.00mm	ISO 75-2/B	91.0 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	90.0 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,4.00mm	ISO 75-2/A	90.0 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	95.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
ash content	ash content --	ISO 3451	25 %
ash content	ash content	ash content --	ASTM D5630	25 %
density	density	ASTM D792	1.39 g/cm³
density	density	density	ISO 1183	1.39 g/cm³
melt mass-flow rate	melt mass-flow rate 250°C/5.0kg	ASTM D1238	37 g/10min
melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 250°C/5.0kg	ISO 1133	37 g/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	ASTM D955	0.18to0.22 %
	Shrinkage rate	Shrinkage rate TD：3.20mm	ASTM D955	0.18to0.22 %
		Shrinkage rate	Shrinkage rate TD:3.20mm	ISO 2577	0.18to0.22 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD:3.20mm	ISO 2577	0.18to0.22 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	110
Rockwell hardness	Rockwell hardness R-Scale	ISO 2039-2	110

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

110

Rockwell hardness

R-Scale

ISO 2039-2

110

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.