PC Generic PC - Carbon Fiber Generic

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ASTM D256	340to730 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180	5.3to9.3 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	48to120 J/m
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	22to50 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	6.0to10 kJ/m²
Dart impact	Dart impact 23°C	ASTM D3763	9.40to18.7 J
Dart impact	Dart impact	Dart impact 23°C	ISO 6603-2	1.20to104 J
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	20to39 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Break,23°C	ISO 527-2	88.3to152 MPa
tensile strength	tensile strength	tensile strength 23°C	ASTM D638	95.7to165 MPa
elongation	elongation Yield,23°C	ASTMD638	1.5to3.1 %
	elongation	elongation Break,23°C	ASTM D638	0.90to3.8 %
	elongation	elongation	elongation Break,23°C	ISO 527-2	1.0to2.7 %
Bending modulus	Bending modulus 23°C	ASTM D790	5700to17000 MPa
tensile strength	tensile strength Break,23°C	ASTM D638	91.6to152 MPa
	tensile strength	tensile strength Yield,23°C	ISO 527-2	56.4to144 MPa
	tensile strength	tensile strength	tensile strength Yield,23°C	ASTM D638	87.8to148 MPa
bending strength	bending strength Break,23°C	ASTM D790	154to260 MPa
bending strength	bending strength	bending strength Yield,23°C	ASTM D790	146to177 MPa
Tensile modulus	Tensile modulus 23°C	ISO 527-2	6900to18200 MPa
Friction coefficient	Friction coefficient	ASTM D1894	0.12to0.55
Tensile modulus	Tensile modulus 23°C	ASTM D638	6760to19700 MPa
Bending modulus	Bending modulus 23°C	ISO 178	5870to16500 MPa
bending strength	bending strength 23°C	ASTM D790	137to243 MPa
bending strength	bending strength	bending strength 23°C	ISO 178	139to227 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ASTM D696	7.0E-6到5.8E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	9.6E-6到4.2E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ASTME831	1.2E-5到1.0E-4 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ISO 11359-2	4.1E-5到6.1E-5 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD	ASTME831	1.1E-5到7.6E-5 cm/cm/°C
RTI	RTI	UL 746	80.0to81.0 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	139to151 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	140to152 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	137to152 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	134to148 °C
Continuous use temperature	Continuous use temperature	ASTM D794	130 °C
Vicat softening temperature	Vicat softening temperature	ISO 306	151to160 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ASTM D696	1.0E-6到3.3E-5 cm/cm/°C
thermal conductivity	thermal conductivity 23°C	ISO 8302	0.30to0.47 W/m/K
RTI Elec	RTI Elec	UL 746	80.0to81.0 °C
RTI Imp	RTI Imp	UL 746	80.0to81.3 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density --	ASTM D1505	1.24to1.37 g/cm³
	density	density 23°C	ISO 1183	1.23to1.42 g/cm³
	density	density	density --	ASTM D792	1.22to1.40 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/1.2kg	ISO 1133	3.40to10.1 cm³/10min
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ISO 1133	1.1to18 g/10min
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.095to0.21 %
Shrinkage rate	Shrinkage rate MD:23°C	ASTM D955	0.066to0.32 %
	Shrinkage rate	Shrinkage rate TD:23°C	ASTM D955	0.28to0.50 %
	Shrinkage rate	Shrinkage rate	Shrinkage rate 23°C	ISO 294-4	0.065to0.51 %
Water absorption rate	Water absorption rate 23°C,24hr	ASTM D570	0.076to0.15 %
	Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.14to0.20 %
	Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.070to0.30 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity 23°C	ASTM D257	5.0到2.5E+8 ohms·cm
Surface resistivity	Surface resistivity --	IEC 60093	5.5到1.3E+11 ohms
Surface resistivity	Surface resistivity	Surface resistivity --	ASTM D257	2.5到6.3E+10 ohms
Volume resistivity	Volume resistivity 23°C	IEC 60093	0.50到1.0E+4 ohms·cm
insulation resistance	insulation resistance 23°C	IEC 60167	1.0E+2到2.5E+7 ohms

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness 23°C	ASTM D785	118to120

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

23°C

ASTM D785

118to120

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.