PC Generic PC - Carbon Fiber Generic
--
--
--
- -
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Thông số kỹ thuật

impact performanceĐiều kiện kiểm traPhương pháp kiểm traGeneric/Generic PC - Carbon Fiber
Suspended wall beam without notch impact strength23°CASTM D256340to730 J/m
Impact strength of cantilever beam gap23°CISO 1805.3to9.3 kJ/m²
Dart impact23°CISO 6603-21.20to104 J
Charpy Notched Impact Strength23°CISO 1796.0to10 kJ/m²
Suspended wall beam without notch impact strength23°CISO 18020to39 kJ/m²
Impact strength of cantilever beam gap23°CASTM D25648to120 J/m
Dart impact23°CASTM D37639.40to18.7 J
Impact strength of simply supported beam without notch23°CISO 17922to50 kJ/m²
mechanical propertiesĐiều kiện kiểm traPhương pháp kiểm traGeneric/Generic PC - Carbon Fiber
Friction coefficientASTM D18940.12to0.55
Tensile modulus23°CASTM D6386760to19700 MPa
tensile strengthBreak,23°CASTM D63891.6to152 MPa
elongationYield,23°CASTMD6381.5to3.1 %
tensile strengthYield,23°CISO 527-256.4to144 MPa
bending strengthYield,23°CASTM D790146to177 MPa
elongationBreak,23°CISO 527-21.0to2.7 %
tensile strengthBreak,23°CISO 527-288.3to152 MPa
bending strength23°CASTM D790137to243 MPa
tensile strengthYield,23°CASTM D63887.8to148 MPa
Tensile modulus23°CISO 527-26900to18200 MPa
Bending modulus23°CISO 1785870to16500 MPa
tensile strength23°CASTM D63895.7to165 MPa
Bending modulus23°CASTM D7905700to17000 MPa
elongationBreak,23°CASTM D6380.90to3.8 %
bending strength23°CISO 178139to227 MPa
Break,23°CASTM D790154to260 MPa
thermal performanceĐiều kiện kiểm traPhương pháp kiểm traGeneric/Generic PC - Carbon Fiber
Hot deformation temperature1.8MPa,UnannealedASTM D648137to152 °C
RTI ElecUL 74680.0to81.0 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B140to152 °C
Linear coefficient of thermal expansionMDASTME8311.2E-5到1.0E-4 cm/cm/°C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A134to148 °C
Linear coefficient of thermal expansionMDASTM D6961.0E-6到3.3E-5 cm/cm/°C
RTIUL 74680.0to81.0 °C
Hot deformation temperature0.45MPa,UnannealedASTM D648139to151 °C
thermal conductivity23°CISO 83020.30to0.47 W/m/K
Linear coefficient of thermal expansionTDASTM D6967.0E-6到5.8E-5 cm/cm/°C
RTI ImpUL 74680.0to81.3 °C
Continuous use temperatureASTM D794130 °C
Linear coefficient of thermal expansionTDISO 11359-24.1E-5到6.1E-5 cm/cm/°C
Vicat softening temperatureISO 306151to160 °C
Linear coefficient of thermal expansionMDISO 11359-29.6E-6到4.2E-5 cm/cm/°C
TDASTME8311.1E-5到7.6E-5 cm/cm/°C
Physical propertiesĐiều kiện kiểm traPhương pháp kiểm traGeneric/Generic PC - Carbon Fiber
melt mass-flow rate300°C/1.2kgISO 11331.1to18 g/10min
Water absorption rateEquilibrium,23°C,50%RHISO 620.095to0.21 %
density--ASTM D15051.24to1.37 g/cm³
Shrinkage rateTD:23°CASTM D9550.28to0.50 %
density23°CISO 11831.23to1.42 g/cm³
Shrinkage rateMD:23°CASTM D9550.066to0.32 %
23°CISO 294-40.065to0.51 %
Water absorption rate23°C,24hrASTM D5700.076to0.15 %
Saturation,23°CISO 620.070to0.30 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11333.40to10.1 cm³/10min
Water absorption rate23°C,24hrISO 620.14to0.20 %
density--ASTM D7921.22to1.40 g/cm³
Electrical performanceĐiều kiện kiểm traPhương pháp kiểm traGeneric/Generic PC - Carbon Fiber
insulation resistance23°CIEC 601671.0E+2到2.5E+7 ohms
Surface resistivity--IEC 600935.5到1.3E+11 ohms
Volume resistivity23°CASTM D2575.0到2.5E+8 ohms·cm
23°CIEC 600930.50到1.0E+4 ohms·cm
Surface resistivity--ASTM D2572.5到6.3E+10 ohms
hardnessĐiều kiện kiểm traPhương pháp kiểm traGeneric/Generic PC - Carbon Fiber
Rockwell hardness23°CASTM D785118to120