ASA+PC GELOY™ XTPMFR10 resin SABIC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	ISO 6603-2	85.0 J
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	13 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 0°C	ISO 180/1A	12 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	330 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	90 J/m
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	13 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.0mm	UL 94	V-0

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.0mm

UL 94

V-0

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	2680 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	2680 MPa
tensile strength	tensile strength Yield	ASTM D638	60.0 MPa
	tensile strength	tensile strength Yield	ASTM D638	65.0 MPa
		tensile strength	tensile strength Break	ISO 527-2/50	47.0 MPa
		tensile strength	tensile strength	tensile strength Break	ISO 527-2/5	46.0 MPa
bending strength	bending strength	ISO 178	97.0 MPa
tensile strength	tensile strength Break4	ASTM D638	47.0 MPa
	tensile strength	tensile strength Break3	ASTM D638	49.0 MPa
		tensile strength	tensile strength Yield	ISO 527-2/50	66.0 MPa
		tensile strength	tensile strength	tensile strength Yield	ISO 527-2/5	61.0 MPa
Bending modulus	Bending modulus	ISO 178	2730 MPa
Tensile strain	Tensile strain Break	ISO 527-2/50	21 %
Tensile strain	Tensile strain	Tensile strain Break	ISO 527-2/5	50 %
elongation	elongation Break4	ASTM D638	31 %
elongation	elongation	elongation Break3	ASTM D638	58 %
Tensile strain	Tensile strain Yield	ISO 527-2/50	4.0 %
Tensile strain	Tensile strain	Tensile strain Yield	ISO 527-2/5	4.0 %
elongation	elongation Yield	ASTM D638	4.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	96.0 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	98.0 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	81.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	90.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	6.3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	6.3E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
MeltViscosity	MeltViscosity 260°C,1500sec^-1	ISO 11443	105 Pa·s
density	density	ISO 1183	1.18 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 260°C/2.16kg	ISO 1133	30.0 cm³/10min

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

MeltViscosity

260°C,1500sec^-1

ISO 11443

105 Pa·s

density

ISO 1183

1.18 g/cm³

Melt Volume Flow Rate (MVR)

260°C/2.16kg

ISO 1133

30.0 cm³/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.