impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	48 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	49 kJ/m²

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of simply supported beam without notch

-30°C

ISO 179/1eU

48 kJ/m²

Impact strength of simply supported beam without notch

23°C

ISO 179/1eU

49 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	V-2
	UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating 0.38mm	IEC 60695-11-10,-20	V-2
			UL flame retardant rating	UL flame retardant rating 0.75mm	IEC 60695-11-10,-20	V-2
				UL flame retardant rating	UL flame retardant rating 1.5mm	IEC 60695-11-10,-20	V-2
				UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.0mm	IEC 60695-11-10,-20	V-2
Burning wire flammability index	Burning wire flammability index 0.38mm	IEC 60695-2-12	850 °C
	Burning wire flammability index	Burning wire flammability index 0.75mm	IEC 60695-2-12	850 °C
		Burning wire flammability index	Burning wire flammability index 1.5mm	IEC 60695-2-12	960 °C
		Burning wire flammability index	Burning wire flammability index	Burning wire flammability index 3.0mm	IEC 60695-2-12	960 °C
Burning rate	Burning rate 0.380mm,Self-Extinguishing	ISO 3795	0.0 mm/min
	Burning rate	Burning rate 0.750mm,Self-Extinguishing	ISO 3795	0.0 mm/min
		Burning rate	Burning rate 1.50mm,自动灭火	ISO 3795	0.0 mm/min
		Burning rate	Burning rate	Burning rate 3.00mm,自动灭火	ISO 3795	0.0 mm/min
UL flame retardant rating	UL flame retardant rating 0.38mm	UL 94	V-2
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 0.75mm	UL 94	V-2
Hot filament ignition temperature	Hot filament ignition temperature 0.38mm	IEC 60695-2-13	825 °C
	Hot filament ignition temperature	Hot filament ignition temperature 0.75mm	IEC 60695-2-13	825 °C
		Hot filament ignition temperature	Hot filament ignition temperature 1.5mm	IEC 60695-2-13	825 °C
		Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 3.0mm	IEC 60695-2-13	825 °C
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	23 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1A/1	3800 Mpa
tensile strength	tensile strength Yield	ISO 527-2/1A/50	70.0 Mpa
Tensile strain	Tensile strain Yield	ISO 527-2/1A/50	3.0 %

mechanical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Tensile modulus

ISO 527-2/1A/1

3800 Mpa

tensile strength

Yield

ISO 527-2/1A/50

70.0 Mpa

Tensile strain

Yield

ISO 527-2/1A/50

3.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/Bf	186 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/Af	76.0 °C
RTI Imp	RTI Imp 3.0mm	UL 746	100 °C
RTI Str	RTI Str 0.38mm	UL 746	100 °C
	RTI Str	RTI Str 0.75mm	UL 746	110 °C
		RTI Str	RTI Str 1.5mm	UL 746	120 °C
		RTI Str	RTI Str	RTI Str 3.0mm	UL 746	120 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	217 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	202 °C
Ball Pressure Test	Ball Pressure Test 200°C	IEC 60695-10-2	Pass
RTI Elec	RTI Elec 0.38mm	UL 746	130 °C
	RTI Elec	RTI Elec 0.75mm	UL 746	130 °C
		RTI Elec	RTI Elec 1.5mm	UL 746	130 °C
		RTI Elec	RTI Elec	RTI Elec 3.0mm	UL 746	130 °C
RTI Imp	RTI Imp 0.38mm	UL 746	75.0 °C
	RTI Imp	RTI Imp 0.75mm	UL 746	90.0 °C
	RTI Imp	RTI Imp	RTI Imp 1.5mm	UL 746	100 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Stickiness	Stickiness	ISO 307	145 cm³/g

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Stickiness

ISO 307

145 cm³/g

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	V
High arc combustion index	High arc combustion index 0.38mm	UL 746	PLC 0
	High arc combustion index	High arc combustion index 0.75mm	UL 746	PLC 0
		High arc combustion index	High arc combustion index 1.5mm	UL 746	PLC 0
		High arc combustion index	High arc combustion index	High arc combustion index 3.0mm	UL 746	PLC 0
Hot wire ignition	Hot wire ignition 0.38mm	UL 746	PLC 4
	Hot wire ignition	Hot wire ignition 0.75mm	UL 746	PLC 4
		Hot wire ignition	Hot wire ignition 1.5mm	UL 746	PLC 2
		Hot wire ignition	Hot wire ignition	Hot wire ignition 3.0mm	UL 746	PLC 0

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test H358/30	ISO 2039-1	160 Mpa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

H358/30

ISO 2039-1

160 Mpa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.