impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	52 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ASTM D256	110 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	800 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180/1A	8.4 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	41 kJ/m²
Dart impact	Dart impact -40°C,TotalEnergy	ASTM D3763	50.0 J
Dart impact	Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	50.0 J

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	5VA
Burning wire flammability index	Burning wire flammability index 1.0mm	IEC 60695-2-12	960 °C
Burning wire flammability index	Burning wire flammability index	Burning wire flammability index 3.0mm11	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature 1.0mm	IEC 60695-2-13	825 °C
Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 3.0mm	IEC 60695-2-13	725 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	2200 MPa
Bending modulus	Bending modulus	ISO 178	2130 MPa
bending strength	bending strength	ISO 178	73.0 MPa
bending strength	bending strength	bending strength Yield,50.0mmSpan	ASTM D790	80.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	2100 MPa
tensile strength	tensile strength Yield	Internal Method	48.0 MPa
	tensile strength	tensile strength Yield	ASTM D638	53.0 MPa
		tensile strength	tensile strength Yield	ISO 527-2/50	51.0 MPa
			tensile strength	tensile strength Break	ASTM D638	43.0 MPa
			tensile strength	tensile strength	tensile strength Break	ISO 527-2/50	40.0 MPa
elongation	elongation Yield	ASTM D638	5.0 %
Tensile strain	Tensile strain Yield	ISO 527-2/50	4.0 %
elongation	elongation Break	Internal Method	250 %
elongation	elongation	elongation Break3	ASTM D638	50 %
Tensile strain	Tensile strain Break	ISO 527-2/50	42 %
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2200 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	8.8E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	9E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	9E-05 cm/cm/°C
RTI Elec	RTI Elec	UL 746	120 °C
RTI Imp	RTI Imp	UL 746	120 °C
RTI Str	RTI Str	UL 746	120 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,6.40mm	ASTM D648	119 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	75.0 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	96.0 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	77.0 °C
Vicat softening temperature	Vicat softening temperature	ASTM D152510	105 °C
	Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	122 °C
	Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	124 °C
Ball Pressure Test	Ball Pressure Test 125°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	8.8E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.030 %
Outdoor applicability	Outdoor applicability	UL 746C	f1
density	density	ISO 1183	1.30 g/cm³
melt mass-flow rate	melt mass-flow rate 265°C/2.16kg	ASTM D1238	11 g/10min
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 265°C/2.16kg	ISO 1133	9.00 cm³/10min
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.70to1.0 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.10 %
density	density	ASTM D792	1.30 g/cm³

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	ASTM D257	6E+16 ohms
Dissipation factor	Dissipation factor 1MHz	ASTM D150	0.020

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Surface resistivity

ASTM D257

6E+16 ohms

Dissipation factor

1MHz

ASTM D150

0.020

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.