PA66 Vydyne® R535J NT0665 Ascend Performance Materials Operations LLC

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	11 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	12 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	68 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	79 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -30°C	ISO 180	11 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180	12 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot filament ignition temperature	Hot filament ignition temperature 3.0mm	IEC 60695-2-13	750 °C
	Hot filament ignition temperature	Hot filament ignition temperature 1.5mm	IEC 60695-2-13	725 °C
	Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 0.75mm	IEC 60695-2-13	775 °C
Burning wire flammability index	Burning wire flammability index 0.75mm	IEC 60695-2-12	750 °C
	Burning wire flammability index	Burning wire flammability index 1.5mm	IEC 60695-2-12	725 °C
	Burning wire flammability index	Burning wire flammability index	Burning wire flammability index 3.0mm	IEC 60695-2-12	800 °C
UL flame retardant rating	UL flame retardant rating 0.75mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating 1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	UL flame retardant rating 3.0mm	UL 94	HB

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
bending strength	bending strength 23°C	ISO 178	300 MPa
Bending modulus	Bending modulus 23°C	ISO 178	10500 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2	2.8 %
tensile strength	tensile strength Break,23°C	ISO 527-2	209 MPa
Tensile modulus	Tensile modulus 23°C	ISO 527-2	11600 MPa
Poisson's Ratio	Poisson's Ratio 23°C	ISO 527	0.40

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
RTI Str	RTI Str 3.0mm	UL 746	125 °C
	RTI Str	RTI Str 1.5mm	UL 746	125 °C
	RTI Str	RTI Str	RTI Str 0.75mm	UL 746	125 °C
RTI Imp	RTI Imp 3.0mm	UL 746	105 °C
	RTI Imp	RTI Imp 1.5mm	UL 746	100 °C
	RTI Imp	RTI Imp	RTI Imp 0.75mm	UL 746	100 °C
RTI Elec	RTI Elec 3.0mm	UL 746	120 °C
	RTI Elec	RTI Elec 1.5mm	UL 746	120 °C
	RTI Elec	RTI Elec	RTI Elec 0.75mm	UL 746	120 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：23to55°C	ISO 11359-2	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：23to55°C	ISO 11359-2	2.1E-05 cm/cm/°C
Melting temperature	Melting temperature	ISO 11357-3	260 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	261 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	251 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate TD:2.00mm	ISO 294-4	0.90 %
density	density 23°C	ISO 1183	1.41 g/cm³
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	1.6 %
Shrinkage rate	Shrinkage rate MD:2.00mm	ISO 294-4	0.40 %
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.80 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dielectric strength	Dielectric strength 1.00mm	IEC 60243	20 kV/mm
Volume resistivity	Volume resistivity 0.750mm	IEC 60093	1E+14 ohms·cm
High arc combustion index	High arc combustion index 0.75mm	UL 746	PLC 0
	High arc combustion index	High arc combustion index 1.5mm	UL 746	PLC 0
	High arc combustion index	High arc combustion index	High arc combustion index 3.0mm	UL 746	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index 3.00mm	IEC 60112	PLC 0
Arc resistance	Arc resistance 3.00mm	ASTM D495	PLC 5
High voltage arc tracing rate	High voltage arc tracing rate HVTR	UL 746	PLC 1
Hot wire ignition	Hot wire ignition 0.75mm	UL 746	PLC 4
	Hot wire ignition	Hot wire ignition 1.5mm	UL 746	PLC 4
	Hot wire ignition	Hot wire ignition	Hot wire ignition 3.0mm	UL 746	PLC 3

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Automotive Materials	Automotive Materials thicknessd=1mm	FMVSS302	+

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Automotive Materials

thicknessd=1mm

FMVSS302

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.