mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
elongation	elongation Yield	ASTM D638	5.0 %
tensile strength	tensile strength Yield	ASTM D638	56.5 Mpa
Tensile modulus	Tensile modulus	ASTM D638	2210 Mpa
bending strength	bending strength Yield,50.0mmSpan	ASTM D790	86.2 Mpa
Bending modulus	Bending modulus 50.0mmSpan	ASTM D790	2340 Mpa
elongation	elongation Break	ASTM D638	150 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
thermal conductivity	thermal conductivity	ASTMC177	0.20 W/m/K
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	7.2E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,6.40mm	ASTM D648	110 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	107 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	124 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C	ASTM D570	0.40 %
Water absorption rate	Water absorption rate	Water absorption rate 24hr	ASTM D570	0.10 %
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.50-0.70 %
melt mass-flow rate	melt mass-flow rate 260°C/5.0kg	ASTM D1238	9.0 g/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.