PC LUBEXAN GF40 NATURAL LUBEN PLAST srl

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	8.0to14 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.20mm	ASTM D256A	140to150 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C3	ASTM D256	45to55 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C4	ASTM D256	14to15 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/A	8.0to14 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180	50to60 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	50to60 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1A/1	9000to9500 MPa
tensile strength	tensile strength Yield	ISO 527-2/1A/5	105to115 MPa
tensile strength	tensile strength	tensile strength Break	ISO 527-2/1A/5	105to115 MPa
Tensile strain	Tensile strain Yield	ISO 527-2/1A/5	1.0to1.5 %
Tensile strain	Tensile strain	Tensile strain Break	ISO 527-2/1A/5	1.0to1.5 %
Bending modulus	Bending modulus	ISO 178	6300to6800 MPa
bending strength	bending strength	ISO 178	175to185 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	135to145 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	140to150 °C
	Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	125to135 °C
Glass transition temperature	Glass transition temperature	Internal Method	140to150 °C
Vicat softening temperature	Vicat softening temperature --	ISO 306/A120	145to155 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/B120	135to145 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183/A	1.43to1.47 g/cm³

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

ISO 1183/A

1.43to1.47 g/cm³

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.