PP PP TM 40-1 Poly Plastic

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 20°C		20 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -40°C		6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 20°C		3.0 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 20°C		20 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -40°C		6.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 20°C		3.0 kJ/m²

mechanical properties	Điều kiện kiểm tra	Kết quả kiểm tra
bending strength	bending strength	45.0 MPa
Bending modulus	Bending modulus 23°C	3700 MPa
Tensile strain	Tensile strain Break	37 %
tensile strength	tensile strength Yield	30.0 MPa
Tensile strain	Tensile strain Break	37 %
tensile strength	tensile strength Yield	30.0 MPa
bending strength	bending strength	45.0 MPa
Bending modulus	Bending modulus 23°C	3700 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature Melting Temperature		164 °C
	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed		75.0 °C
		Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed		125 °C
			Hot deformation temperature	Hot deformation temperature 线形热膨胀系数-Flow(-20to110°C)		6E-06 cm/cm/°C
				Hot deformation temperature	Hot deformation temperature Melting Temperature		164 °C
					Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed		75.0 °C
						Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed		125 °C
						Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 线形热膨胀系数-Flow(-20to110°C)		6E-06 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Kết quả kiểm tra
density	density	1.24 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	2.6 g/10min
Shrinkage rate	Shrinkage rate	0.40to0.60 %
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	2.6 g/10min
density	density	1.24 g/cm³
Shrinkage rate	Shrinkage rate	0.40to0.60 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity		1E+15 ohms·cm
Volume resistivity	Volume resistivity		1E+15 ohms·cm

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Volume resistivity

1E+15 ohms·cm

Volume resistivity

1E+15 ohms·cm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.