POM/GF/PTFE LNP™ LUBRICOMP™ KFL4016NC SABIC INNOVATIVE US

186

Đặc tính:
Chịu nhiệt độ caoChống tia cực tím
Lĩnh vực ứng dụng:
Trang chủTrang chủ
So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dart impact	Dart impact 23°C, Energy at Peak	ASTM D3763	9.00 J
Dart impact	Dart impact	Dart impact --	ISO 6603-2	2.00 J
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C3	ISO 180/1U	17 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ASTM D4812	210 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Wear factor	Wear factor	ASTM D3702	1.9E+8 10^-8 mm³/N·m
Friction coefficient	Friction coefficient Static	ASTM D3702	0.43
Friction coefficient	Friction coefficient	Friction coefficient Dynamic	ASTM D3702	0.50
bending strength	bending strength	ASTM D790	92.0 Mpa
Bending modulus	Bending modulus --	ISO 178	6300 Mpa
Bending modulus	Bending modulus	Bending modulus --	ASTM D790	5300 Mpa
elongation	elongation Break	ISO 527-2	4.0 %
	elongation	elongation Break	ASTM D638	2.6 %
		elongation	elongation Yield	ISO 527-2	2.3 %
		elongation	elongation	elongation Yield	ASTM D638	3.6 %
tensile strength	tensile strength Break	ISO 527-2	46.0 Mpa
	tensile strength	tensile strength Break	ASTM D638	56.0 Mpa
		tensile strength	tensile strength Yield	ISO 527-2	49.0 Mpa
		tensile strength	tensile strength	tensile strength Yield	ASTM D638	56.0 Mpa
Tensile modulus	Tensile modulus --	ISO 527-2/1	5800 Mpa
Tensile modulus	Tensile modulus	Tensile modulus --1	ASTM D638	6130 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	210 to 220 °C
Processing (melt) temperature	Processing (melt) temperature	200 to 215 °C
Mold temperature	Mold temperature	80 to 110 °C
Back pressure	Back pressure	0.200 to 0.300 Mpa
Screw speed	Screw speed	30 to 60 rpm
drying temperature	drying temperature	80 °C
drying time	drying time	4.0 hr
Temperature at the rear of the barrel	Temperature at the rear of the barrel	175 to 190 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	195 to 205 °C

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 3.20 mm	ASTM D648	161 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	132 °C
Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span3	ISO 75-2/Af	147 °C

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hot deformation temperature

0.45 MPa, Unannealed, 3.20 mm

ASTM D648

161 °C

Hot deformation temperature

1.8 MPa, Unannealed, 3.20 mm

ASTM D648

132 °C

Hot deformation temperature

1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span3

ISO 75-2/Af

147 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium, 23°C, 50% RH	ISO 62	0.29 %
Water absorption rate	Water absorption rate	Water absorption rate 24 hr, 50% RH	ASTM D570	0.16 %
Shrinkage rate	Shrinkage rate Flow : 24hr	ISO 294-4	1.5 %
	Shrinkage rate	Shrinkage rate 横向Flow : 24hr	ISO 294-4	1.3 %
		Shrinkage rate	Shrinkage rate Across FlowFlow : 24hr	ASTM D955	1.6 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate Flow : 24hr	ASTM D955	1.4 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.