Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap --	ASTM D256	390 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -10°C	ASTM D256	150 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap --	ASTM D256	390 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -10°C	ASTM D256	150 J/m

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield	ASTM D638	20.6 MPa
elongation	elongation Break	ASTM D638	300 %
Bending modulus	Bending modulus	ASTM D790A	2260 MPa
tensile strength	tensile strength Yield	ASTM D638	20.6 MPa
elongation	elongation Break	ASTM D638	300 %
Bending modulus	Bending modulus	ASTM D790A	2260 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	130 °C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	130 °C

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hot deformation temperature

0.45MPa,Unannealed

ASTM D648

130 °C

Hot deformation temperature

0.45MPa,Unannealed

ASTM D648

130 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	1.08 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ASTM D1238	20 g/10min
Shrinkage rate	Shrinkage rate MD	ASTM D955	0.80 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ASTM D955	0.75 %
density	density	ASTM D792	1.08 g/cm³
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ASTM D1238	20 g/10min
Shrinkage rate	Shrinkage rate MD	ASTM D955	0.80 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ASTM D955	0.75 %

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	72
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	72

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

Rockwell hardness

R-Scale

ASTM D785

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Processing temperature	Processing temperature		210to230 °C
Processing temperature	Processing temperature		210to230 °C

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Processing temperature

210to230 °C

Processing temperature

210to230 °C

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.