PP HiFill® PP GF20 Techmer Polymer Modifiers

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.18mm	ASTM D256	110 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 3.18mm	ASTM D256	590 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C,3.18mm	ASTM D256	110 J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 3.18mm	ASTM D256	590 J/m

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating	UL 94	HB
UL flame retardant rating	UL flame retardant rating	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

UL 94

UL flame retardant rating

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus	ASTM D790	2930 MPa
bending strength	bending strength	ASTM D790	79.3 MPa
tensile strength	tensile strength Break	ASTM D638	48.3 MPa
tensile strength	tensile strength	tensile strength Break	ASTM D638	48.3 MPa
elongation	elongation Break	ASTM D638	4.0 %
elongation	elongation	elongation Break	ASTM D638	4.0 %
Bending modulus	Bending modulus	ASTM D790	2930 MPa
bending strength	bending strength	ASTM D790	79.3 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melting temperature	Melting temperature		163 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ASTM D696	3.4E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	163 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	154 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ASTM D696	3.4E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	163 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ASTM D648	154 °C
Melting temperature	Melting temperature		163 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate 24hr	ASTM D570	0.010 %
density	density	ASTM D792	1.04 g/cm³
Shrinkage rate	Shrinkage rate MD：3.18mm	ASTM D955	0.40 %
Water absorption rate	Water absorption rate 24hr	ASTM D570	0.010 %
density	density	ASTM D792	1.04 g/cm³
Shrinkage rate	Shrinkage rate MD：3.18mm	ASTM D955	0.40 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dielectric strength	Dielectric strength	ASTM D149	21 kV/mm
Volume resistivity	Volume resistivity	ASTM D257	4E+16 ohms·cm
Volume resistivity	Volume resistivity	Volume resistivity	ASTM D257	4E+16 ohms·cm
Dielectric strength	Dielectric strength	ASTM D149	21 kV/mm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	112
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	112

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

112

Rockwell hardness

R-Scale

ASTM D785

112

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.