PC WONDERLOY® PC-510 CHI MEI CORPORATION
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179 | 15 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179 | 45 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C,3.18mm | ASTM D256 | 590 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180 | 15 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180 | 45 kJ/m² |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| UL flame retardant rating | UL flame retardant rating 2.1mm | UL 94 | 5VB |
| UL flame retardant rating | UL flame retardant rating 1.5mm | UL 94 | V-0 |
| UL flame retardant rating | UL flame retardant rating 3.0mm | UL 94 | 5VA |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| bending strength | bending strength | ISO 178 | 80.0 MPa |
| bending strength | bending strength 23°C | ASTM D790 | 78.5 MPa |
| Bending modulus | Bending modulus | ISO 178 | 2500 MPa |
| Bending modulus | Bending modulus 23°C | ASTM D790 | 245 MPa |
| Tensile strain | Tensile strain Break | ISO 527-2/50 | 110 % |
| Tensile strain | Tensile strain Break,23°C | ASTM D638 | 100 % |
| tensile strength | tensile strength Break | ISO 527-2/50 | 45.0 MPa |
| tensile strength | tensile strength Yield | ISO 527-2/50 | 55.0 MPa |
| tensile strength | tensile strength Yield,23°C | ASTM D638 | 49.0 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to55°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 85.0 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/A50 | 94.0 °C |
| Vicat softening temperature | Vicat softening temperature -- | ASTM D152511 | 85.0 °C |
| Vicat softening temperature | Vicat softening temperature -- | ASTM D152510 | 94.0 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,3.20mm | ASTM D648 | 78.0 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,6.40mm | ASTM D648 | 87.0 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,4.00mm | ISO 75-2/A | 73.0 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Spiral flow length | Spiral flow length | Internal Method | 45.0 cm |
| Shrinkage rate | Shrinkage rate MD | ASTM D955 | 0.40to0.60 % |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 260°C/2.16kg | ISO 1133 | 21.0 cm³/10min |
| melt mass-flow rate | melt mass-flow rate 260°C/2.16kg | ASTM D1238 | 20 g/10min |
| density | density 23°C | ISO 1183 | 1.17 g/cm³ |
| density | density | ASTM D792 | 1.17 g/cm³ |
| Shrinkage rate | Shrinkage rate | ISO 2577 | 0.40to0.60 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Dielectric constant | Dielectric constant 1MHz | IEC 60250 | 3.10 |
| Volume resistivity | Volume resistivity | IEC 60093 | 3.9E+19 ohms·cm |
| Surface resistivity | Surface resistivity | IEC 60093 | 2.9E+17 ohms |
| hardness | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Rockwell hardness | Rockwell hardness R-Sale,23°C | ASTM D785 | 113 |
| Rockwell hardness | Rockwell hardness R-Sale,23°C | ISO 2039-2 | 113 |