PP Witcom PP 2008/003 Witcom Engineering Plastics B.V.

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	ISO 180/1U	45 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ISO 180/1A	15 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	ISO 180/1U	45 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ISO 180/1A	15 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 3.0mm	ISO 1210	HB
UL flame retardant rating	UL flame retardant rating 3.0mm	ISO 1210	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

3.0mm

ISO 1210

UL flame retardant rating

3.0mm

ISO 1210

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield	ISO 527-2	<80.0 MPa
Tensile strain	Tensile strain Break	ISO 527-2	2.0to4.0 %
tensile strength	tensile strength Yield	ISO 527-2	<80.0 MPa
bending strength	bending strength	ISO 178	115 MPa
Bending modulus	Bending modulus	ISO 178	6000 MPa
bending strength	bending strength	ISO 178	115 MPa
Bending modulus	Bending modulus	ISO 178	6000 MPa
Tensile strain	Tensile strain Break	ISO 527-2	2.0to4.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
RTI Imp	RTI Imp 3.0mm	UL 746	75.0 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	4.5E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	140 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	4.5E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	140 °C
RTI Imp	RTI Imp 3.0mm	UL 746	75.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.020 %
Shrinkage rate	Shrinkage rate MD：3.00mm	ISO 2577	0.30to0.50 %
density	density	ISO 1183	1.27 g/cm³
density	density	density	ISO 1183	1.27 g/cm³
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.010 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.010 %
Shrinkage rate	Shrinkage rate MD：3.00mm	ISO 2577	0.30to0.50 %
Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.020 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	ASTM D257	10到1.0E+3 ohms
Surface resistivity	Surface resistivity	ASTM D257	10到1.0E+3 ohms

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Surface resistivity

ASTM D257

10到1.0E+3 ohms

Surface resistivity

ASTM D257

10到1.0E+3 ohms

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.