impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	6.7 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ISO 180/1U	35 kJ/m²
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	ISO 6603-2	2.10 J
Dart impact	Dart impact 23°C,EnergyatPeakLoad	ASTM D3763	7.60 J

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus	ISO 178	5800 Mpa
bending strength	bending strength	ASTM D790	179 Mpa
bending strength	bending strength	bending strength	ISO 178	183 Mpa
Friction coefficient	Friction coefficient Dynamic	ASTM D3702Modified	0.40
Friction coefficient	Friction coefficient	Friction coefficient Static	ASTM D3702Modified	0.45
Wear factor	Wear factor Washer	ASTM D3702Modified	19.5 10^-10in^5-min/ft-lb-hr
Tensile modulus	Tensile modulus	ASTM D638	6890 Mpa
Tensile modulus	Tensile modulus	Tensile modulus	ISO 527-2/1	6440 Mpa
tensile strength	tensile strength Yield	ASTM D638	120 Mpa
tensile strength	tensile strength	tensile strength Yield	ISO 527-2	118 Mpa
Bending modulus	Bending modulus	ASTM D790	5520 Mpa
Tensile strain	Tensile strain Break	ISO 527-2	3.1 %
elongation	elongation Break	ASTM D638	3.1 %
Tensile strain	Tensile strain Yield	ISO 527-2	3.1 %
elongation	elongation Yield	ASTM D638	3.1 %
tensile strength	tensile strength Break	ISO 527-2	118 Mpa
tensile strength	tensile strength	tensile strength Break	ASTM D638	120 Mpa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ISO 11359-2	3.9E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD：-40to40°C	ASTME831	4E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ISO 11359-2	8.3E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-40to40°C	ASTME831	8.3E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	243 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,3.20mm	ASTM D648	261 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed,3.20mm	ASTM D648	247 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	260 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate MD：24hr	ASTM D955	0.50-0.70 %
	Shrinkage rate	Shrinkage rate TD：24hr	ASTM D955	1.6-1.8 %
		Shrinkage rate	Shrinkage rate TD:24hr	ISO 294-4	1.7 %
		Shrinkage rate	Shrinkage rate	Shrinkage rate MD:24hr	ISO 294-4	0.64 %
Water absorption rate	Water absorption rate 24hr,50%RH	ASTM D570	0.60 %

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.