PBT+PET TechnoDur PBT/PET GF 30 Natural (9966) TECHNOCOMPOUND GERMANY

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	10 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	60 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	65 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 0.8mm	Internal Method	HB
Burning wire flammability index	Burning wire flammability index 2.0mm	IEC 60695-2-12	750 °C

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

0.8mm

Internal Method

Burning wire flammability index

2.0mm

IEC 60695-2-12

750 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1	10500 MPa
tensile strength	tensile strength Break	ISO 527-2/5	155 MPa
Tensile strain	Tensile strain Break	ISO 527-2/5	2.5 %
Bending modulus	Bending modulus	ISO 178	9000 MPa
bending strength	bending strength --	ISO 178	220 MPa
bending strength	bending strength	bending strength 3.5%Strain	ISO 178	210 MPa
Bending strain	Bending strain	ISO 178	3.0 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	220 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD:23to80°C	ISO 11359-2	3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion TD:23to80°C	ISO 11359-2	6E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	205 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 8.0MPa,Unannealed	ISO 75-2/C	125 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	225 °C
Melting temperature	Melting temperature	ISO 11357-3	220to255 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.55 g/cm³
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 265°C/2.16kg	ISO 1133	14.0 cm³/10min
Shrinkage rate	Shrinkage rate TD	ISO 2577	0.90 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 2577	0.30 %
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.20 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.40 %
Viscosity value	Viscosity value 降低的粘度	ISO 1628	106.4 ml/g

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 60093	1E+15 ohms
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm
Dielectric strength	Dielectric strength 1.00mm	IEC 60243-1	28 kV/mm
Relative permittivity	Relative permittivity 100Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	Relative permittivity 1MHz	IEC 60250	3.80
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 2

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	220 MPa

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

ISO 2039-1

220 MPa

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.