Filling analysis	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Melt density	Melt density		1.40 g/cm³
Top out temperature	Top out temperature		210 °C
Specific Heat Capacity of Melt	Specific Heat Capacity of Melt		1870 J/kg/°C
Thermal Conductivity of Melt	Thermal Conductivity of Melt		0.31 W/m/K
Emission of Organic Compounds	Emission of Organic Compounds	VDA 277	6.50 µgC/g
Odor	Odor	VDA 270	3.00

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	90 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	100 kJ/m²

impact performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Impact strength of simply supported beam without notch

-30°C

ISO 179/1eU

90 kJ/m²

Impact strength of simply supported beam without notch

23°C

ISO 179/1eU

100 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating	UL 94	HB
UL flame retardant rating	UL flame retardant rating	UL flame retardant rating	UL 94	HB
Extreme Oxygen Index	Extreme Oxygen Index	ISO 4589-2	24 %
FMVSS combustion rate	FMVSS combustion rate	FMVSS 302	SE
雾化 - G-value (condensate)	雾化 - G-value (condensate)	ISO 6452	4.0E-4 g

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2	17000 Mpa
tensile strength	tensile strength Break	ISO 527-2	250 Mpa
Tensile strain	Tensile strain Break	ISO 527-2	2.3 %
Tensile creep modulus	Tensile creep modulus 1 hr	ISO 899-1	-- Mpa
Tensile creep modulus	Tensile creep modulus	Tensile creep modulus 1000 hr	ISO 899-1	-- Mpa

injection	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature		80 °C
Drying time - hot air dryer	Drying time - hot air dryer		2.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content		0.20 %
Processing (melt) temperature	Processing (melt) temperature		285 to 305 °C
Melt Temperature, Optimum	Melt Temperature, Optimum		295 °C
Mold temperature	Mold temperature		50 to 90 °C
Mold Temperature, Optimum	Mold Temperature, Optimum		100 °C
Maintain pressure	Maintain pressure		50.0 to 100 Mpa
Maintain pressure	Maintain pressure	Maintain pressure Drying Recommended		yes
Hold Pressure Time	Hold Pressure Time		3.00 s/mm
Maximum Screw Tangential Speed	Maximum Screw Tangential Speed		12 m/min

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed	ISO 75-2/B	262 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed	ISO 75-2/A	260 °C
Glass transition temperature	Glass transition temperature	ISO 11357-2	80.0 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	255 °C
Melting temperature	Melting temperature	ISO 11357-3	262 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Flow	ISO 11359-2	1.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion Across Flow	ISO 11359-2	7.5E-5 cm/cm/°C
thermal conductivity	thermal conductivity		0.46 W/m/K

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate 横向Flow	ISO 294-4	0.80 %
Shrinkage rate	Shrinkage rate	Shrinkage rate Flow	ISO 294-4	0.30 %
Water absorption rate	Water absorption rate Saturation, 23°C, 2.00 mm	ISO 62	4.2 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.2 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Surface resistivity	Surface resistivity	IEC 62631-3-2	-- ohms
Volume resistivity	Volume resistivity	IEC 62631-3-1	1.0E+13 ohms·m

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Surface resistivity

IEC 62631-3-2

-- ohms

Volume resistivity

IEC 62631-3-1

1.0E+13 ohms·m

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.