impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	20 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	500 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap -25°C	ISO 180/1A	10 kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/1A	12 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	V-2
Hot filament ignition temperature	Hot filament ignition temperature 2.0mm	IEC 60695-2-13	850 °C
Extreme Oxygen Index	Extreme Oxygen Index	ASTM D2863	26 %

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.6mm

UL 94

V-2

Hot filament ignition temperature

2.0mm

IEC 60695-2-13

850 °C

Extreme Oxygen Index

ASTM D2863

26 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1	2300 MPa
tensile strength	tensile strength Yield	ISO 527-2/50	60.0 MPa
Tensile strain	Tensile strain Break	ISO 527-2/50	80 %
Bending modulus	Bending modulus	ISO 178	2500 MPa
bending strength	bending strength	ISO 178	80.0 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Vicat softening temperature	Vicat softening temperature	ISO 306/A50	148 °C
Ball Pressure Test	Ball Pressure Test 135°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD：-30to30°C	ASTM D696	7E-05 cm/cm/°C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	135 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density 23°C	ISO 1183	1.20 g/cm³
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ISO 1133	22 g/10min
Shrinkage rate	Shrinkage rate TD	ISO 294-4	0.50to0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.50to0.70 %
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.14 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ISO 62	0.30 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dielectric strength	Dielectric strength 2.00mm	IEC 60243-1	20 kV/mm
Compared to the anti leakage trace index	Compared to the anti leakage trace index SolutionA	IEC 60112	PLC 3
Volume resistivity	Volume resistivity	IEC 60093	>1.0E+15 ohms·cm

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Dielectric strength

2.00mm

IEC 60243-1

20 kV/mm

Compared to the anti leakage trace index

SolutionA

IEC 60112

PLC 3

Volume resistivity

IEC 60093

>1.0E+15 ohms·cm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.