thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ASTM D648	73.9 °C
Brittle temperature	Brittle temperature	ASTM D746	<-75.0 °C
Vicat softening temperature	Vicat softening temperature	ASTM D1525	127 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ASTM D696	1.4E-04 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	0.953 g/cm³
melt mass-flow rate	melt mass-flow rate 190°C/2.16kg	ASTM D1238	0.25 g/10min
Environmental stress cracking resistance	Environmental stress cracking resistance F50	ASTM D1693A	45.0 hr

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

ASTM D792

0.953 g/cm³

melt mass-flow rate

190°C/2.16kg

ASTM D1238

0.25 g/10min

Environmental stress cracking resistance

F50

ASTM D1693A

45.0 hr

Supplementary Information	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Mold temperature	Mold temperature		71to88 °C
Forming temperature	Forming temperature		149to177 °C

Supplementary Information

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Mold temperature

71to88 °C

Forming temperature

149to177 °C

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.