PP Homopolymer Advanced-PP 1101P Advanced Petrochemical Company

So sánh

Bảng thông số kỹ thuật

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield,23°C	ISO 527-2	35 MPa
Elongation at Break	Elongation at Break Yield,23°C	ISO 527-2	>=10 %
Elongation at Break	Elongation at Break	Elongation at Break 23°C	ISO 527-2	50 %
Tensile modulus	Tensile modulus 23°C	ISO 527-2	1550 MPa
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	3.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	Charpy Notched Impact Strength -30°C	ISO 179/1eA	1.5 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	105 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch -30°C	ISO 179/1eU	15 kJ/m²

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion MD	ISO 11359-2	1.4E-04 cm/cm／°C
Melting temperature	Melting temperature		163 °C
Hot deformation temperature	Hot deformation temperature 0.45MPaUnannealed	ISO 75-2/Bf	85 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.80MPaUnannealed	ISO 75-2/Af	55 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/A50	92 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	0.910 g/cm³
Water absorption rate	Water absorption rate 23°C,24hr	ISO 62	0.10 %
Water absorption rate	Water absorption rate	Water absorption rate 23°C,50RH	ISO 62	0.10 %
melt mass-flow rate	melt mass-flow rate 230℃/2.16Kg	ISO 1133	26 g/10min

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	>=1.0E+15 Ω.cm
Surface resistivity	Surface resistivity	IEC 60093	1E+14 Ω.cm
Dielectric strength	Dielectric strength	IEC 60243-1	140 KV/mm
Dielectric constant	Dielectric constant	IEC 60250	2.3 1MHz
Dissipation factor	Dissipation factor	IEC 60250	0.00020 1MHz
Compared to the anti leakage trace index	Compared to the anti leakage trace index	IEC 60112	PLC 0

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.