SMMA NAS® 21 INEOS Barex

So sánh

Bảng thông số kỹ thuật

optical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Refractive index	Refractive index	ASTM D542	1.570
Refractive index	Refractive index	Refractive index	ISO 489	1.570
transmissivity	transmissivity 550nm	ASTM D1003	91.3 %
turbidity	turbidity	ASTM D1003	0.30 %

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	1.5 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	ISO 180	12 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ISO 180/A	2.5 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap 23°C	ASTM D256	21 J/m
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	12 kJ/m²

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Bending modulus	Bending modulus	ASTM D790	3100 MPa
Bending modulus	Bending modulus	Bending modulus	ISO 178	3400 MPa
bending strength	bending strength	ASTM D790	97.2 MPa
bending strength	bending strength	bending strength	ISO 178	100 MPa
Tensile strain	Tensile strain Break,23°C	ISO 527-2	2.5 %
elongation	elongation Break	ASTM D638	2.1 %
tensile strength	tensile strength Yield,23°C	ISO 527-2	60.0 MPa
tensile strength	tensile strength	tensile strength Yield,23°C	ASTM D638	57.9 MPa
Tensile modulus	Tensile modulus	ISO 527-2	3300 MPa
Tensile modulus	Tensile modulus	Tensile modulus	ASTM D638	3240 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Maximum operating temperature	Maximum operating temperature		260 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	98.0 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature	ASTM D15253	106 °C
Hot deformation temperature	Hot deformation temperature 1.8MPa,Annealed	ISO 75-2/A	80.0 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	90.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Water absorption rate	Water absorption rate Equilibrium,23°C,50%RH	ISO 62	0.10 %
Water absorption rate	Water absorption rate	Water absorption rate Saturation,23°C	ASTM D570	0.10 %
Shrinkage rate	Shrinkage rate	ISO 294-4	0.20to0.60 %
Shrinkage rate	Shrinkage rate	Shrinkage rate MD	ASTM D955	0.20to0.60 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 220°C/10.0kg	ISO 1133	24.0 cm³/10min
melt mass-flow rate	melt mass-flow rate 200°C/5.0kg	ASTM D1238	1.9 g/10min
density	density	ISO 1183	1.08 g/cm³
density	density	density	ASTM D792	1.08 g/cm³

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Ball Pressure Test	Ball Pressure Test	ISO 2039-1	168 MPa
Rockwell hardness	Rockwell hardness M-Scale	ASTM D785	70

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Ball Pressure Test

ISO 2039-1

168 MPa

Rockwell hardness

M-Scale

ASTM D785

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.