Bảng thông số kỹ thuật
impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
---|---|---|---|
Dart impact | Dart impact 23°C,TotalEnergy | ASTM D3763 | 55.0 J |
Dart impact | Dart impact -30°C,TotalEnergy | ASTM D3763 | 67.0 J |
Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/1A | 65 kJ/m² |
Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180/1A | 30 kJ/m² |
Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 65 kJ/m² |
Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179/1eA | 30 kJ/m² |
mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
---|---|---|---|
Tensile modulus | Tensile modulus | ASTM D638 | 2300 Mpa |
Tensile modulus | Tensile modulus | ISO 527-2/1 | 2250 Mpa |
tensile strength | tensile strength Yield | ASTM D638 | 54.0 Mpa |
elongation | elongation Yield | ASTM D638 | 4.5 % |
tensile strength | tensile strength Break | ISO 527-2/50 | 53.0 Mpa |
tensile strength | tensile strength Break | ASTM D638 | 53.0 Mpa |
tensile strength | tensile strength Yield | ISO 527-2/50 | 54.0 Mpa |
bending strength | bending strength Yield,50.0mmSpan | ASTM D790 | 89.0 Mpa |
bending strength | bending strength | ISO 178 | 82.0 Mpa |
Bending modulus | Bending modulus | ISO 178 | 2200 Mpa |
Bending modulus | Bending modulus 50.0mmSpan | ASTM D790 | 2300 Mpa |
Tensile strain | Tensile strain Break | ISO 527-2/50 | 120 % |
elongation | elongation Break | ASTM D638 | 120 % |
Tensile strain | Tensile strain Yield | ISO 527-2/50 | 4.5 % |
thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
---|---|---|---|
Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 126 °C |
Vicat softening temperature | Vicat softening temperature -- | ISO 306/B120 | 127 °C |
Ball Pressure Test | Ball Pressure Test 75°C | IEC 60695-10-2 | Pass |
Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD:-40to40°C | ASTME831 | 7E-05 cm/cm/°C |
Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD:-40to40°C | ISO 11359-2 | 8E-05 cm/cm/°C |
thermal conductivity | thermal conductivity | ISO 8302 | 0.20 W/m/K |
Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD:-40to40°C | ISO 11359-2 | 8E-05 cm/cm/°C |
Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD:-40to40°C | ASTME831 | 7E-05 cm/cm/°C |
Vicat softening temperature | Vicat softening temperature | ASTM D152510 | 126 °C |
Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 105 °C |
Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,3.20mm | ASTM D648 | 107 °C |
Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 126 °C |
Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
---|---|---|---|
melt mass-flow rate | melt mass-flow rate 260°C/5.0kg | ASTM D1238 | 26 g/10min |
Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 260°C/5.0kg | ISO 1133 | 22.0 cm3/10min |
Shrinkage rate | Shrinkage rate MD:3.20mm | Internal Method | 0.50-0.70 % |
Shrinkage rate | Shrinkage rate TD:3.20mm | Internal Method | 0.50-0.70 % |
Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 0.40 % |
Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 0.15 % |
MeltViscosity | MeltViscosity 260°C,1500sec^-1 | ISO 11443 | 170 Pa·s |
Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
---|---|---|---|
Volume resistivity | Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm |
Dielectric strength | Dielectric strength 0.800mm,in Oil | IEC 60243-1 | 35 KV/mm |
Dielectric strength | Dielectric strength 1.60mm,in Oil | IEC 60243-1 | 25 KV/mm |
Dielectric strength | Dielectric strength 3.20mm,in Oil | IEC 60243-1 | 17 KV/mm |
Surface resistivity | Surface resistivity | IEC 60093 | >1.0E+15 ohms |