	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ISO 1183	1.13 g/cm³
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	102 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	121 °C
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	45 kJ/m²
bending strength	bending strength	ISO 178	82.0 MPa
Bending modulus	Bending modulus 23°C	ISO 178	2500 MPa
Tensile strain	Tensile strain Yield	ISO 527-2	7.0 %
tensile strength	tensile strength	ISO 527-2	48.0 MPa
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	HB
Vicat softening temperature	Vicat softening temperature --	ISO 306/B50	123 °C
Vicat softening temperature	Vicat softening temperature	Vicat softening temperature --	ISO 306/A50	136 °C
Shrinkage rate	Shrinkage rate MD	ISO 294-4	0.50to0.70 %
Shrinkage rate	Shrinkage rate	Shrinkage rate TD	ISO 294-4	0.50to0.70 %
melt mass-flow rate	melt mass-flow rate 260°C/5.0kg	ISO 1133	20 g/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.