impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Dart impact	Dart impact 23°C,TotalEnergy	ASTM D3763	74.0 J
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength 23°C	ASTM D4812	3200 J/m
Dart impact	Dart impact 23°C	ASTM D3029	149 J
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	ASTM D1822	578 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.47mm	UL 94	HB

flammability

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

1.47mm

UL 94

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
yield	yield	ASTM D790	97.2 MPa
	yield	yield	ASTM D638	65.5 MPa
	yield	yield	yield	ISO 527-2/50	68.0 MPa
crack	crack	ASTM D638	77.9 MPa
crack	crack	crack	ISO 527-2/50	68.0 MPa
yield	yield	ASTM D638	8.0 %
yield	yield	yield	ISO 527-2/50	7.0 %
crack	crack	ASTM D638	78 %
crack	crack	crack	ISO 527-2/50	100 %

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
specific heat	specific heat	ASTMC351	1260 J/kg/°C
RTI	RTI	UL 746	130 °C
RTI Imp	RTI Imp	UL 746	130 °C
RTI Elec	RTI Elec	UL 746	130 °C
thermal conductivity	thermal conductivity	ASTMC177	0.21 W/m/K
flow	flow	ASTME831	6E-05 cm/cm/°C
flow	flow	flow	ASTME831	8.1E-05 cm/cm/°C
transverse	transverse	ASTME831	6E-05 cm/cm/°C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
balance	balance	ISO 62	0.35 %
saturated	saturated	ISO 62	0.16 %
Shrinkage rate	Shrinkage rate MD：3.20mm	Internal Method	0.80to1.0 %
Melt Volume Flow Rate (MVR)	Melt Volume Flow Rate (MVR) 300°C/1.2kg	ISO 1133	2.00 cm³/10min
melt mass-flow rate	melt mass-flow rate 300°C/1.2kg	ASTM D1238	2.0 g/10min
Specific volume	Specific volume	ASTM D792	0.835 cm³/g

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index CTI	UL 746	PLC 3
High arc combustion index	High arc combustion index HAI	UL 746	PLC 3
High voltage arc tracing rate	High voltage arc tracing rate HVTR	UL 746	PLC 3
Hot wire ignition	Hot wire ignition HWI	UL 746	PLC 2
Arc resistance	Arc resistance	ASTM D495	PLC6
Dissipation factor	Dissipation factor 100Hz	ASTM D150	0.026
	Dissipation factor	Dissipation factor 60Hz	ASTM D150	1.6E-03
	Dissipation factor	Dissipation factor	Dissipation factor 50Hz	ASTM D150	1.6E-03
Dielectric constant	Dielectric constant 1MHz	ASTM D150	3.10
	Dielectric constant	Dielectric constant 60Hz	ASTM D150	3.27
	Dielectric constant	Dielectric constant	Dielectric constant 50Hz	ASTM D150	3.27
Dielectric strength	Dielectric strength 3.20mm,inAir	ASTM D149	20 kV/mm
Volume resistivity	Volume resistivity	ASTM D257	>2.5E+17 ohms·cm

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness M-Scale	ASTM D785	92
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	127

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

M-Scale

ASTM D785

Rockwell hardness

R-Scale

ASTM D785

127

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.