PP MAJORIS DFR111R AD MAJORIS FRANCE

So sánh

Bảng thông số kỹ thuật

impact performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	50 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	4.5 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179	50 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179	4.5 kJ/m²

flammability	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	V-2
Hot filament ignition temperature	Hot filament ignition temperature 2.0mm	IEC 60695-2-13	775 °C
Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 1.0mm	IEC 60695-2-13	775 °C
Burning wire flammability index	Burning wire flammability index 1.0mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	Hot filament ignition temperature 2.0mm	IEC 60695-2-13	775 °C
Hot filament ignition temperature	Hot filament ignition temperature	Hot filament ignition temperature 1.0mm	IEC 60695-2-13	775 °C
Burning wire flammability index	Burning wire flammability index 1.0mm	IEC 60695-2-12	960 °C
UL flame retardant rating	UL flame retardant rating 1.6mm	UL 94	V-2

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ISO 527-2/1	2500 MPa
tensile strength	tensile strength Yield	ISO 527-2/50	35.0 MPa
Tensile strain	Tensile strain Break	ISO 527-2/50	>200 %
Tensile strain	Tensile strain	Tensile strain Break	ISO 527-2/50	>200 %
tensile strength	tensile strength Yield	ISO 527-2/50	35.0 MPa
Tensile modulus	Tensile modulus	ISO 527-2/1	2500 MPa

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	68.0 °C
	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	112 °C
		Hot deformation temperature	Hot deformation temperature 1.8MPa,Unannealed	ISO 75-2/A	68.0 °C
		Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 0.45MPa,Unannealed	ISO 75-2/B	112 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	7.0 g/10min
Shrinkage rate	Shrinkage rate	Internal Method	1.4 %
density	density	ISO 1183	0.960 g/cm³
Shrinkage rate	Shrinkage rate	Internal Method	1.4 %
melt mass-flow rate	melt mass-flow rate 230°C/2.16kg	ISO 1133	7.0 g/10min
density	density	ISO 1183	0.960 g/cm³

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.