optical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Refractive index	Refractive index	ISO 489	1.53 °C
Transmittance rate	Transmittance rate 2000μm	ISO 13468-2	91 %
turbidity	turbidity	ISO 13468-2	<=0.1 %
gloss	gloss	ISO 2813	>=100 %

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength 23°C	ISO 527-2	63 Mpa
Elongation at Break	Elongation at Break 23°C	ISO 527-2	4.5 %
Tensile modulus	Tensile modulus 23°C	ISO 527-2	2600 Mpa
Charpy Notched Impact Strength	Charpy Notched Impact Strength 23°C	ISO 179/1eA	2.6 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch 23°C	ISO 179/1eU	20 kJ/m²
Elongation at Break	Elongation at Break MD,23°C	ISO 527-2	2.9 %
Elongation at Break	Elongation at Break	Elongation at Break TD,23°C	ISO 527-2	3 %
Tensile modulus	Tensile modulus TD,23°C	ISO 527-2	1800 Mpa
	Tensile modulus	Tensile modulus MD,23°C	ISO 527-2	2200 Mpa
		Tensile modulus	Tensile modulus Break拉伸强度	ISO 527-3	57 Mpa
			Tensile modulus	Tensile modulus Break拉伸强度	ISO 527-3	50 Mpa
				Tensile modulus	Tensile modulus Elmendorf撕裂强度	ISO 6383-2	225 g
					Tensile modulus	Tensile modulus Elmendorf撕裂强度	ISO 6383-2	230 g
					Tensile modulus	Tensile modulus	Tensile modulus 跌落试验	ISO 7765-1	<=36 g

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45MPaUnannealed	ISO 75-2/Bf	75 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	80 °C
Vicat softening temperature	Vicat softening temperature 玻璃转化温度	ISO 11357-2	78 °C

thermal performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Hot deformation temperature

0.45MPaUnannealed

ISO 75-2/Bf

75 °C

Vicat softening temperature

ISO 306/B50

80 °C

Vicat softening temperature

玻璃转化温度

ISO 11357-2

78 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 260℃/2.16Kg	ISO 1133	32 cm3/10min
Water absorption rate	Water absorption rate (23°C,24hr)	ISO 62	0.01 %
melt mass-flow rate	melt mass-flow rate 190℃/2.16Kg	ISO 1133	1.8 g/10min
	melt mass-flow rate	melt mass-flow rate 230℃/2.16Kg	ISO 1133	11 g/10min
		melt mass-flow rate	melt mass-flow rate 水蒸气渗透性		3.70 gmil/(m2day
			melt mass-flow rate	melt mass-flow rate 氧渗透		997 cm3mil/(m2dayatm
				melt mass-flow rate	melt mass-flow rate 水蒸气穿透率	ISO 15106-3	0.0008 g/m²/day
				melt mass-flow rate	melt mass-flow rate	melt mass-flow rate 厚度		70 microns

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Volume resistivity	Volume resistivity	IEC 60093	1E+14 Ω.cm
Dielectric constant	Dielectric constant 23°C	IEC 60250	2.35 1kHz
Dissipation factor	Dissipation factor 相对漏电起痕指数	IEC 60112	600 V

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Volume resistivity

IEC 60093

1E+14 Ω.cm

Dielectric constant

23°C

IEC 60250

2.35 1kHz

Dissipation factor

相对漏电起痕指数

IEC 60112

600 V

flame retardant performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
UL flame retardant rating	UL flame retardant rating	UL -94	HB 1.50mm

flame retardant performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

UL flame retardant rating

UL -94

HB 1.50mm

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.