PC LEXAN™ 3412ECR resin SABIC
So sánhBảng thông số kỹ thuật
| impact performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch -30°C | ISO 179/1eU | 40 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength 23°C | ISO 179/1eA | 6.0 kJ/m² |
| Charpy Notched Impact Strength | Charpy Notched Impact Strength -30°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | Impact strength of simply supported beam without notch 23°C | ISO 179/1eU | 40 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ASTM D256 | 110 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ASTM D256 | 110 J/m |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap -30°C | ISO 180/1A | 6.0 kJ/m² |
| Impact strength of cantilever beam gap | Impact strength of cantilever beam gap 23°C | ISO 180/1A | 7.0 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength -30°C | ISO 180/1U | 35 kJ/m² |
| Suspended wall beam without notch impact strength | Suspended wall beam without notch impact strength 23°C | ISO 180/1U | 35 kJ/m² |
| Dart impact | Dart impact 23°C,TotalEnergy | ASTM D3763 | 20.0 J |
| flammability | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Burning wire flammability index | Burning wire flammability index 1.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | Hot filament ignition temperature 1.0mm | IEC 60695-2-13 | 825 °C |
| Extreme Oxygen Index | Extreme Oxygen Index | ISO 4589-2 | 40 % |
| UL flame retardant rating | UL flame retardant rating 1.5mm | UL 94 | V-0 |
| UL flame retardant rating | UL flame retardant rating 3.0mm | UL 94 | 5VA |
| mechanical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| elongation | elongation Yield | ASTM D638 | 3.1 % |
| bending strength | bending strength Yield,50.0mmSpan | ASTM D790 | 156 MPa |
| bending strength | bending strength | ISO 178 | 140 MPa |
| Bending modulus | Bending modulus | ISO 178 | 5500 MPa |
| Bending modulus | Bending modulus 50.0mmSpan | ASTM D790 | 5000 MPa |
| Tensile strain | Tensile strain Break | ISO 527-2/5 | 3.2 % |
| Tensile strain | Tensile strain Yield | ISO 527-2/5 | 2.8 % |
| Tensile modulus | Tensile modulus | ASTM D638 | 5500 MPa |
| Tensile modulus | Tensile modulus | ISO 527-2/1 | 6000 MPa |
| tensile strength | tensile strength Yield | ASTM D638 | 90.0 MPa |
| tensile strength | tensile strength Yield | ISO 527-2/5 | 95.0 MPa |
| tensile strength | tensile strength Break | ASTM D638 | 87.0 MPa |
| tensile strength | tensile strength Break | ISO 527-2/5 | 90.0 MPa |
| thermal performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| RTI Str | RTI Str | UL 746 | 130 °C |
| RTI Imp | RTI Imp | UL 746 | 130 °C |
| RTI Elec | RTI Elec | UL 746 | 130 °C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：23to80°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion TD：-40to40°C | ASTME831 | 7E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：23to80°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | Linear coefficient of thermal expansion MD：-40to40°C | ASTME831 | 3E-05 cm/cm/°C |
| Ball Pressure Test | Ball Pressure Test 125°C | IEC 60695-10-2 | Pass |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B120 | 146 °C |
| Vicat softening temperature | Vicat softening temperature -- | ISO 306/B50 | 145 °C |
| Hot deformation temperature | Hot deformation temperature 0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 141 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,3.20mm | ASTM D648 | 141 °C |
| Hot deformation temperature | Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 136 °C |
| Vicat softening temperature | Vicat softening temperature | ASTM D152510 | 147 °C |
| Physical properties | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| density | density | ASTM D792 | 1.30 g/cm³ |
| density | density | ISO 1183 | 1.36 g/cm³ |
| melt mass-flow rate | melt mass-flow rate 300°C/1.2kg | ASTM D1238 | 7.0 g/10min |
| Melt Volume Flow Rate (MVR) | Melt Volume Flow Rate (MVR) 300°C/1.2kg | ISO 1133 | 7.00 cm³/10min |
| Shrinkage rate | Shrinkage rate MD：3.20mm | Internal Method | 0.20to0.50 % |
| Shrinkage rate | Shrinkage rate TD：3.20mm | Internal Method | 0.20to0.50 % |
| Water absorption rate | Water absorption rate Saturation,23°C | ISO 62 | 0.29 % |
| Water absorption rate | Water absorption rate Equilibrium,23°C,50%RH | ISO 62 | 0.12 % |
| Electrical performance | Điều kiện kiểm tra | Phương pháp kiểm tra | Kết quả kiểm tra |
|---|---|---|---|
| Relative permittivity | Relative permittivity 1MHz | IEC 60250 | 3.30 |
| Dissipation factor | Dissipation factor 50Hz | IEC 60250 | 0.020 |
| Dissipation factor | Dissipation factor 60Hz | IEC 60250 | 0.020 |
| Relative permittivity | Relative permittivity 60Hz | IEC 60250 | 3.30 |
| Relative permittivity | Relative permittivity 50Hz | IEC 60250 | 3.30 |
| Volume resistivity | Volume resistivity | IEC 60093 | >1.0E+15 ohms·cm |
| Surface resistivity | Surface resistivity | IEC 60093 | >1.0E+15 ohms |
| Dissipation factor | Dissipation factor 1MHz | IEC 60250 | 0.010 |
| Arc resistance | Arc resistance | ASTM D495 | PLC7 |
| Compared to the anti leakage trace index | Compared to the anti leakage trace index CTI | UL 746 | PLC 3 |
| High arc combustion index | High arc combustion index HAI | UL 746 | PLC 3 |
| High voltage arc tracing rate | High voltage arc tracing rate HVTR | UL 746 | PLC 3 |
| Hot wire ignition | Hot wire ignition HWI | UL 746 | PLC 0 |