Other performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Material barrel temperature	Material barrel temperature		180-185 °C
Dart impact	Dart impact	ASTM D1709	3.40 g/micron
Dart impact	Dart impact	Dart impact	ASTM D1709	170 g
Nozzle opening size	Nozzle opening size		0.100 cm
Inflation ratio (BUR)	Inflation ratio (BUR)		2.0-3.0
temperature range	temperature range		150-185 °C

mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Secant modulus	Secant modulus	ASTM D882	140 MPa
Secant modulus	Secant modulus	Secant modulus	ASTM D882	170 MPa
tensile strength	tensile strength Break	ASTM D882	25.0 MPa
tensile strength	tensile strength	tensile strength Break	ASTM D882	23.0 MPa
Elongation at Break	Elongation at Break	ASTM D882	350 %
Elongation at Break	Elongation at Break	Elongation at Break	ASTM D882	700 %
Elmendorf tear strength	Elmendorf tear strength	ASTM D1922	310 g
	Elmendorf tear strength	Elmendorf tear strength	ASTM D1922	250 g
		Elmendorf tear strength	Elmendorf tear strength	ASTM D1922	6.20 g/micron
		Elmendorf tear strength	Elmendorf tear strength	Elmendorf tear strength	ASTM D1922	5.00 g/micron

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
density	density	ASTM D792	0.924 g/cm³
melt mass-flow rate	melt mass-flow rate 190℃/2.16Kg	ASTM D1238	0.60 g/10min

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

density

ASTM D792

0.924 g/cm³

melt mass-flow rate

190℃/2.16Kg

ASTM D1238

0.60 g/10min

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.