mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Tensile modulus	Tensile modulus	ASTM D638	2270 Mpa
tensile strength	tensile strength Yield	ASTM D638	57.0 Mpa
elongation	elongation Yield	ASTM D638	5.0 %
elongation	elongation	elongation Break	ASTM D638	100 %
Bending modulus	Bending modulus 50.0 mm Span	ASTM D790	2340 Mpa
bending strength	bending strength Yield, 50.0 mm Span	ASTM D790	88.0 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	100 to 110 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.020 %
Suggested injection volume	Suggested injection volume	30 to 80 %
Hopper temperature	Hopper temperature	60 to 80 °C
Temperature at the rear of the barrel	Temperature at the rear of the barrel	250 to 290 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	255 to 295 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	260 to 300 °C
Spray nozzle temperature	Spray nozzle temperature	275 to 300 °C
Processing (melt) temperature	Processing (melt) temperature	275 to 300 °C
Mold temperature	Mold temperature	60 to 90 °C
Back pressure	Back pressure	0.300 to 0.700 Mpa
Screw speed	Screw speed	40 to 70 rpm
Exhaust hole depth	Exhaust hole depth	0.038 to 0.076 mm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 3.20 mm	ASTM D648	129 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 3.20 mm	ASTM D648	112 °C
Vicat softening temperature	Vicat softening temperature	ISO 306/B50	130 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion -40 to 40°C，Flow	ASTM E831	7.2E-5 cm/cm/°C
RTI Elec	RTI Elec	UL 746	105 °C
RTI Imp	RTI Imp	UL 746	80.0 °C
RTI	RTI	UL 746	105 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
melt mass-flow rate	melt mass-flow rate 260°C/5.0 kg	ASTM D1238	19 g/10 min
Shrinkage rate	Shrinkage rate 3.20 mm，Flow	Internal Method	0.50 - 0.70 %

Physical properties

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

melt mass-flow rate

260°C/5.0 kg

ASTM D1238

19 g/10 min

Shrinkage rate

3.20 mm，Flow

Internal Method

0.50 - 0.70 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Compared to the anti leakage trace index	Compared to the anti leakage trace index	UL 746	PLC 2
High arc combustion index	High arc combustion index	UL 746	PLC 1
Hot wire ignition	Hot wire ignition	UL 746	PLC 3

Electrical performance

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Compared to the anti leakage trace index

UL 746

PLC 2

High arc combustion index

UL 746

PLC 1

Hot wire ignition

UL 746

PLC 3

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.