mechanical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
tensile strength	tensile strength Yield	ASTM D638	151 Mpa
tensile strength	tensile strength	tensile strength Break	ASTM D638	158 Mpa
elongation	elongation Break	ASTM D638	7.0 %
Bending modulus	Bending modulus 100 mm Span	ASTM D790	8580 Mpa
bending strength	bending strength Yield, 100 mm Span	ASTM D790	248 Mpa

injection	Điều kiện kiểm tra	Kết quả kiểm tra
drying temperature	drying temperature	95 to 105 °C
drying time	drying time	3.0 to 4.0 hr
Suggested maximum moisture content	Suggested maximum moisture content	0.070 %
Suggested injection volume	Suggested injection volume	30 to 50 %
Temperature at the rear of the barrel	Temperature at the rear of the barrel	265 to 305 °C
Temperature in the middle of the barrel	Temperature in the middle of the barrel	270 to 305 °C
Temperature at the front of the material cylinder	Temperature at the front of the material cylinder	275 to 305 °C
Spray nozzle temperature	Spray nozzle temperature	280 to 305 °C
Processing (melt) temperature	Processing (melt) temperature	280 to 305 °C
Mold temperature	Mold temperature	75 to 120 °C
Back pressure	Back pressure	0.300 to 1.40 Mpa
Screw speed	Screw speed	20 to 100 rpm
Exhaust hole depth	Exhaust hole depth	0.013 to 0.038 mm

thermal performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Hot deformation temperature	Hot deformation temperature 0.45 MPa, Unannealed, 6.40 mm	ASTM D648	254 °C
Hot deformation temperature	Hot deformation temperature	Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm	ASTM D648	240 °C
Vicat softening temperature	Vicat softening temperature	ASTM D15255	248 °C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion -20 to 150°C，Flow	ASTM E831	2.0E-5 - 3.1E-5 cm/cm/°C
RTI Elec	RTI Elec	UL 746	50.0 °C
RTI Imp	RTI Imp	UL 746	50.0 °C
RTI	RTI	UL 746	50.0 °C

Physical properties	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Shrinkage rate	Shrinkage rate Flow : 3.20 mm	Internal Method	0.20 - 0.30 %
Shrinkage rate	Shrinkage rate	Shrinkage rate Across FlowFlow : 3.20 mm	Internal Method	0.65 - 0.85 %
Water absorption rate	Water absorption rate 24 hr, 50% RH	ASTM D570	0.50 %
Water absorption rate	Water absorption rate	Water absorption rate Equilibrium, 50% RH	ASTM D570	1.0 %

Electrical performance	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Arc resistance	Arc resistance	ASTM D495	PLC 6
Compared to the anti leakage trace index	Compared to the anti leakage trace index	UL 746	PLC 2
High arc combustion index	High arc combustion index	UL 746	PLC 2
High voltage arc tracing rate	High voltage arc tracing rate	UL 746	PLC 1
Hot wire ignition	Hot wire ignition	UL 746	PLC 0

hardness	Điều kiện kiểm tra	Phương pháp kiểm tra	Kết quả kiểm tra
Rockwell hardness	Rockwell hardness R-Scale	ASTM D785	120

hardness

Điều kiện kiểm tra

Phương pháp kiểm tra

Kết quả kiểm tra

Rockwell hardness

R-Scale

ASTM D785

120

Tuyên bố miễn trừ trách nhiệm: Các dữ liệu cung cấp trên website được vnplas.com thu thập từ nhà sản xuất nguyên vật liệu và các nhà cung cấp trung gian. Vnplas.com đã nỗ lực hết sức để đảm bảo tính chính xác của dữ liệu này. Tuy nhiên, chúng tôi không chịu bất kỳ trách nhiệm nào về dữ liệu và khuyến nghị quý doanh nghiệp xác minh dữ liệu với các nhà cung cấp trước khi đưa ra quyết định cuối cùng.